The present invention discloses a high performance aluminum alloy strip and its fabrication method. Its composition is as follows: Si 0.01-0.10%, Fe 0.01-0.30%, Cu < 0.05%, Mn 0.10-0.30%, Mg 2.50-3.50%, Ti < 0.01%, Cr < 0.05%, V < 0.008%, B < 0.008%, Al and inevitable impurities. In the process of smelting and holding, the raw materials are degassed and filtered for many times, and homogenized after semi-continuous casting, sawing and milling, then hot-rolled out of furnace, and then hot-rolled coil is made by cleaning and straightening. The aluminum alloy strip has good welding and deformation properties, high elongation and conductivity, and certain strength.
【技术实现步骤摘要】
一种高性能铝合金带材及其制备方法
本专利技术具体涉及一种高性能铝合金带材及其制作方法。
技术介绍
气体绝缘金属封闭输电线路（GIL）是一种采用SF6或SF6-N2气体绝缘，外壳与导体同轴布置的高电压、大电流电力传输设备，其具有传输容量大、损耗小、电容电流小、占地少、可靠性高等优点，国内近年来开始得到逐步应用。该电线路设计是将铝板带进行卷筒后焊接成外壳，再在焊合后的密封管路内通入SF6或SF6-N2气体作为绝缘介质。因此所用管道需要承压，这就要求制作该管道的铝板带需要有良好的强度及焊接性。同时，密封管道壳体因受输电线交变电流产生磁场的影响会形成涡流热，为减少涡流热需要壳体材料导电率≥37%IACS。目前市面上铝合金板带材难以既满足延伸率、焊接指标又满足导电率指标，且具有一定的强度。因此，开发该类铝板带材具有较高的附加值。
技术实现思路
为克服现有铝合金带材难以全面满足延伸率、焊接性能、导电率要求并同时具有足够强度的问题，本专利技术提供了一种既具有较好的强度和焊接、变形性能，又具有较高导电率的可供电力行业使用的高性能铝合金带材。为实现上述目的，本专利技术采用如下技术方案：...
【技术保护点】
1. 一种高性能铝合金带材，其特征在于：所含成分按重量百分数计为：Si 0.01~0.10%，Fe 0.01~0.30%，Cu ≤0.05%，Mn 0.10~0.30%，Mg 2.50~3.50%，Ti ≤0.01%，Cr ≤0.05%，V ≤0.008%，B≤0.008%，余量为Al及不可避免的杂质。
【技术特征摘要】
1.一种高性能铝合金带材，其特征在于：所含成分按重量百分数计为：Si0.01~0.10%，Fe0.01~0.30%，Cu≤0.05%，Mn0.10~0.30%，Mg2.50~3.50%，Ti≤0.01%，Cr≤0.05%，V≤0.008%，B≤0.008%，余量为Al及不可避免的杂质。2.一种如权利要求1所述高性能铝合金带材的制作方法，其特征在于：包含以下步骤：（1）按成分配比取铝锭、铝中间合金锭、镁锭和锰剂，将其在熔炼、保温静置过程中进行多道次精炼除气和多级过滤，以提高熔体纯净度，再进行半连续铸造；（2）所得铸锭经锯切、铣面后，于480~580℃保温2~15h进行均匀化热处理；（3）出炉热轧，热轧厚度为2.0~10.0mm，热轧终轧温度为300~350℃；（4）将热轧卷材清洗后，对带材进行变形率为0.1~1.0%的拉伸矫直，即得到具有高可焊性、高延伸率及高导电率的高性能铝合金带材。3.根据权利要求2所述的高性能铝合金带材的制作方法，其特征在于：所述铝锭的纯度为99.70%~99.99%。4.根据权利要求2所述的高性能...
【专利技术属性】
技术研发人员：刘旺，黄瑞银，冉继龙，郑智滨，杨本勇，
申请(专利权)人：中铝东南材料院福建科技有限公司，中铝瑞闽股份有限公司，
类型：发明
国别省市：福建,35
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。