An easy-to-spray coating consisting of 60% epoxy resin, 35% quartz powder, 3% antisettling agent, 2% leveling agent, 55% quartz powder, 15% curing agent, 15% toughening agent, 5% antisettling agent, 5% accelerator, 5% leveling agent, and 30% vapor silica by weight percentage. Fly ash 70%, mix evenly, spraying construction. The invention has the following advantages: solving the shortcomings of poor adhesive force of the coating, easy peeling of the coating, and affecting the anticorrosion quality of the coating. Reduce manufacturing costs. Eliminate environmental pollution in construction.
【技术实现步骤摘要】
一种易喷涂的涂料
本专利技术涉及一种易喷涂的涂料。
技术介绍
传统的陶瓷环氧涂料石英粉能使涂料的粘结力增强,并提高涂层机械强度,还耐腐蚀,抗冲击,但其含量不能高,喷涂时堵塞和磨损喷嘴,造成喷涂困难,石英粉不能均匀分配到涂料涂层中去,降低涂层粘结力,涂层易脱落,影响涂层的防腐质量。石英粉含量低,造成陶瓷环氧涂料的成本高,推广应用受到限制。
技术实现思路
本专利技术的目的在于克服上述的缺陷,提供一种易喷涂的涂料。本专利技术的技术方案是:一种易喷涂的涂料,其特征在于:甲组份按重量百分比计:环氧树脂30-60%,石英粉30-60%,防沉剂1-5%,流平剂1-5%,乙组份:石英粉40-70%,固化剂10-25%,增韧剂5-20%,防沉剂1-5%,246二甲基苯酚(DMP-30)促进剂1-5%,流平剂1-5%,甲乙组份混合比例1∶1,防沉剂组份重量百分比为:气相二氧化硅10-30%,粉煤灰30-70,使用方法:在对钢铁的管道进行防腐处理时,先将要处理的表面清扫干净,再将事先配置好的甲、乙组份以1∶1配比现场混合均匀,喷涂,自然干燥后完成管道的防腐处理。本专利技术具有以下优点:解决了涂料涂层粘结力差、涂层易脱落,影响涂层的防腐质量的缺点。降低制造成本。消除施工中的环境污染。具体实施方式实施例1:一种易喷涂的涂料,甲组份按重量百分比计:环氧树脂30%,石英粉65%,防沉剂3%,流平剂2%,乙组份按重量白分比计:石英粉65%,固化剂15%,增韧剂12%,防沉剂5%,促进剂2%,流平剂1%,防沉剂组份构成按重量百分比为:气相二氧化硅30%,粉煤灰70%,将配置好的甲乙组份以1∶1 ...
【技术保护点】
1.一种易喷涂的涂料,其特征在于:甲组份按重量百分比计: 环氧树脂30%,石英粉65%,防沉剂3%,流平剂2%,乙组份按重量白 分比计:石英粉65%,固化剂15%,增韧剂12%,防沉剂5%,促进剂 2%,流平剂1%,防沉剂组份构成按重量百分比为:气相二氧化硅30%, 粉煤灰70%,将配置好的甲乙组份以1∶1比例混合均匀后,喷涂施工。
【技术特征摘要】
1.一种易喷涂的涂料,其特征在于:甲组份按重量百分比计:环氧树脂30%,石英粉65%,防沉剂3%,流平剂2%,乙组份按重量白分比计:石英粉65%,固化剂15%,增...