The invention discloses an intermediate temperature paste aluminum alloy solder and a preparation method thereof. It belongs to the field of aluminum alloy brazing technology. The composition and proportion of the filler metal are as follows: aluminium alloy filler metal powder 400 g, QJ201 flux 60-65 g, liquid paraffin oil 100-110 mL, polyvinylpyrrolidone 2-2.2 G. The solder melting point is lower than 490 C and the brazing temperature is 500 ~ 520 C. It is suitable for brazing aluminum alloy with solid wire higher than 500 C. There are furnace brazing, induction brazing, flame brazing and so on. The brazing joint is brazed to 5A06 aluminum alloy, and the shear strength of the brazed joint is more than 73MPa.
【技术实现步骤摘要】
一种中温膏状铝合金钎料及其制备方法
本专利技术涉及铝合金钎焊
，尤其涉及一种中温膏状铝合金钎料及其制备方法。
技术介绍
铝合金由于具有密度小、比强度高、耐蚀性好等优点，广泛应用于航空航天、石化、汽车、船舶、机械、电力、家用电器等领域。铝合金可采用的焊接方法很多，其中钎焊是最重要的焊接方法之一，它具有钎焊件变形小、尺寸精度高等优点，在实际生产中得到越来越广泛的应用，特别适合于制造复杂的铝合金构件。传统的铝合金钎焊所采用的焊接材料为粉状钎剂与粉、丝、箔、片、棒状等铝合金钎料，但随着钎焊工件的不断小型化，钎焊缝形状的不断多样化以及工业自动化程度的不断提高，传统的钎焊材料已不能完全满足现代工业发展的要求，膏状钎料应运而生，其具有独特优点：(1)便于精确添加钎料，尤其适合形状不规则的钎焊缝；(2)钎剂与钎料配比准确；(3)钎料添加工艺适合于工业自动化生产。因此，膏状钎料具有广阔的应用前景。迄今为止，国内外膏状钎料的研究与开发主要集中在锡基、铜基和银基钎料，膏状铝合金钎料非常少，商品化的屈指可数，且由于膏状钎料中的钎料粉为Al-Si基钎料粉，因此，钎料的熔点较高(Al-...
【技术保护点】
1.一种中温膏状铝合金钎料，其特征在于，钎料组分及配比为：低熔点高强度铝合金粉末钎料400g、粉状钎剂QJ20160～65g、液体石蜡油100～110mL、聚乙烯吡咯烷酮2～2.2g。所述低熔点高强度铝合金粉末钎料由Si、Cu、Ge、Ni、Zn、Sr、Bi、La、Ce、Yb、Al组成，其中Si的质量分数为8.6％～9.5％、Cu的质量分数为16.5％～17.5％、Ge的质量分数为8.5％～9.5％、Ni的质量分数为4.5％～5.0％、Zn的质量分数为4.0％～5.0％、Sr的质量分数为0.70％～0.75％、Bi的质量分数为0.35％～0.40％、La的质量分数为0.40％...
【技术特征摘要】
1.一种中温膏状铝合金钎料，其特征在于，钎料组分及配比为：低熔点高强度铝合金粉末钎料400g、粉状钎剂QJ20160～65g、液体石蜡油100～110mL、聚乙烯吡咯烷酮2～2.2g。所述低熔点高强度铝合金粉末钎料由Si、Cu、Ge、Ni、Zn、Sr、Bi、La、Ce、Yb、Al组成，其中Si的质量分数为8.6％～9.5％、Cu的质量分数为16.5％～17.5％、Ge的质量分数为8.5％～9.5％、Ni的质量分数为4.5％～5.0％、Zn的质量分数为4.0％～5.0％、Sr的质量分数为0.70％～0.75％、Bi的质量分数为0.35％～0.40％、La的质量分数为0.40％～0.45％、Ce的质量分数为0.40％～0.55％、Yb的质量分数为0.10％～0.20％、其...
【专利技术属性】
技术研发人员：罗伟，严密，楼圆，周健，吴琛，
申请(专利权)人：浙江大学，
类型：发明
国别省市：浙江,33