The invention relates to a new flux cored wire for aluminum brazing, which comprises a sheath and a medicine core. The amount of aluminium brazing agent can be adjusted by adjusting the proportion of aluminum filler powder and aluminum filler powder in the core, without adding aluminum filler and changing the outer skin size of the flux cored wire. The method of adjusting the content of aluminum solders can only be changed by changing the size of the outer skin. It is easy to adjust, low in cost, and has good wettability and spreading property for aluminum alloy. It can realize continuous automatic welding and is suitable for popularization and application.
【技术实现步骤摘要】
一种新型铝钎料药芯焊丝
本专利技术涉及焊接领域，尤其涉及一种新型铝钎料药芯焊丝。
技术介绍
铝钎料实心焊丝在使用过程中需另加铝钎剂，使用不方便，生产效率低。普通铝钎料药芯焊丝只能通过改变药芯焊丝外皮尺寸来调节钎料的铝钎剂含量，但改变外皮尺寸还需更换相应配套的生产设备并调整生产工艺，成本较高。
技术实现思路
有鉴于此，本专利技术提供一种解决或部分解决上述问题的新型铝钎料药芯焊丝。为达到上述技术方案的效果，本专利技术的技术方案为：一种新型铝钎料药芯焊丝，包括外皮和药芯，外皮包裹住药芯；新型铝钎料药芯焊丝的直径的范围是1.0mm～3.0mm；外皮为铝钎料合金，外皮的化学成分及其重量百分比为:Si:4.5～13.0％，Cu:0～5.0％，Mg:0～2.0％，Zn:0～3.0％，Fe:0～0.8％，Mn:0～0.15％，Ti：0～0.2％，Cr：0～0.15％，Bi：0～0.2％，余量为Al；药芯包括铝钎料粉与铝钎剂粉，铝钎料粉与铝钎剂粉的配比可调节；铝钎料粉的重量百分比的范围是5～30％，余量为铝钎剂粉；铝钎料粉的化学成分及其重量百分比与外皮的化学成分及其重量百分比一致。新型...
【技术保护点】
1.一种新型铝钎料药芯焊丝，其特征在于，包括：所述新型铝钎料药芯焊丝包括外皮和药芯，所述外皮包裹住所述药芯；所述新型铝钎料药芯焊丝的直径的范围是1.0mm～3.0mm；所述外皮为铝钎料合金，所述外皮的化学成分及其重量百分比为:Si:4.5～13.0％，Cu:0～5.0％，Mg:0～2.0％，Zn:0～3.0％，Fe:0～0.8％，Mn:0～0.15％，Ti：0～0.2％，Cr：0～0.15％，Bi：0～0.2％，余量为Al；所述药芯包括铝钎料粉与铝钎剂粉，所述铝钎料粉与所述铝钎剂粉的配比可调节；所述铝钎料粉的重量百分比的范围是5～30％，余量为所述铝钎剂粉；所述铝钎料粉的化...
【技术特征摘要】
1.一种新型铝钎料药芯焊丝，其特征在于，包括：所述新型铝钎料药芯焊丝包括外皮和药芯，所述外皮包裹住所述药芯；所述新型铝钎料药芯焊丝的直径的范围是1.0mm～3.0mm；所述外皮为铝钎料合金，所述外皮的化学成分及其重量百分比为:Si:4.5～13.0％，Cu:0～5.0％，Mg:0～2.0％，Zn:0～3.0％，Fe:0～0.8％，Mn:0～0.15％，Ti：0～0.2％，Cr：0～0.15％，Bi：0～0.2％，余量为Al；所述药芯包括铝钎料粉与铝钎剂粉，所述铝钎料粉与所述铝钎剂粉的配比可调节；所述铝钎料粉的重量百分比的范围是5～30％，余量为所述铝钎剂粉；所述铝钎料粉的化学成分及其重量百分比与所述外皮的化学成分及其重量百分比一致。2.根据权利要求1所述的一种新型铝钎料药芯焊丝，其特征在于，包括：所述新型铝钎料药芯焊丝的检测方法包括以下步...
【专利技术属性】
技术研发人员：石磊，杨学顺，韩勇，王引平，胡兰伟，龚晓彬，
申请(专利权)人：浙江亚通焊材有限公司，
类型：发明
国别省市：浙江,33