A method for restraining hot cracking of castings is described. The shell used for casting is obtained by the following steps: preparation of aqueous solution containing alkaline hydroxides; local impregnation of the shell corresponding to the parts prone to hot cracking of castings by aqueous solution containing alkaline hydroxides; calcination of the shell to obtain local alkaline oxidation. The shell of a thing. The invention has the advantages of simple operation, flexibility and strong reliability; by adjusting the solute composition, concentration and total impregnation amount of the impregnating solution, the content of alkaline oxide in the mold shell is controlled, the formation of glass phase in the mold shell at high temperature is increased, the concessionality of the mold shell is effectively improved, and the occurrence of metal hot cracking defects is inhibited.
【技术实现步骤摘要】
一种抑制铸件热裂的方法
本专利技术涉及机械
，具体涉及一种抑制铸件热裂的方法。
技术介绍
熔模铸造是用蜡制作所要铸成零件的蜡模，然后蜡模上涂以泥浆形成泥模，并在制泥模时留下浇注口。泥模晾干后，放入热水中将内部蜡模熔化。将熔化完蜡模的泥模取出再焙烧成陶模。再从浇注口灌入金属熔液进行铸造。铸件热裂是熔模铸造中最常见的铸造缺陷之一，尤其是航空领域内使用的钛铝合金，热裂倾向十分明显。热裂主要由合金性质和铸型阻力引起，目前是通过改善铸件结构，改变合金成分来抑制热裂的发生，但是这些措施限制了铸件结构设计和成分设计的自由度。而一些铸件的结构和成分严格，例如部分航空钛铝合金铸件对结构要求和成分要求十分严格，不能轻易改变。因此，热裂缺陷一直是困扰从业人员的关键问题。
技术实现思路
为了解决上述存在的技术问题，本专利技术的目的在于提供一种抑制铸件热裂的方法，以解决熔模铸造中铸件尤其是钛铝合金铸件容易热裂的问题，其具有可操作简单、方法灵活、可靠性高等特点。为达到以上技术目的，本专利技术采用如下技术方案：一种抑制铸件热裂的方法，采用以下步骤获得用于铸造铸件的型壳：制备含有碱性氢氧化物的...
【技术保护点】
1.一种抑制铸件热裂的方法，其特征在于，采用以下步骤获得用于铸造铸件的型壳：制备含有碱性氢氧化物的水溶液；使用含有碱性氢氧化物的水溶液对铸件容易出现热裂的部位对应的第二型壳部位进行局部浸渍；焙烧型壳，使得第二型壳部位含有碱性氧化物。
【技术特征摘要】
1.一种抑制铸件热裂的方法，其特征在于，采用以下步骤获得用于铸造铸件的型壳：制备含有碱性氢氧化物的水溶液；使用含有碱性氢氧化物的水溶液对铸件容易出现热裂的部位对应的第二型壳部位进行局部浸渍；焙烧型壳，使得第二型壳部位含有碱性氧化物。2.根据权利要求1所述的抑制铸件热裂的方法，其特征在于，在制备含有碱性氢氧化物的水溶液之前还包括以下步骤：将造孔剂混入撒砂材料；在铸件容易出现热裂的部位对应的第一型壳部位，使用混有造孔剂的撒砂材料进行撒砂操作，使得第一型壳部位含有造孔剂；焙烧型壳，使得第一型壳部位含有孔洞。3.根据权利要求2所述的抑制铸件热裂的方法，其特征在于，所述造孔剂包括淀粉或有机纤维，添加量为0.01％-20％质量分数。4.根据权利要求1所述的抑制铸件热裂的方法，其特...
【专利技术属性】
技术研发人员：吕志刚，魏亚蒙，胡可辉，李欣怡，
申请(专利权)人：清华大学，
类型：发明
国别省市：北京,11