The invention discloses a processing method of silk sponge, the first step is: pressing the silk sponge to be processed into a high-pressure and high-temperature pot; the second step is: adding penetrant and formic acid into the pot, then heating and pressurizing; the third step is: opening the pot cover, adding methacrylamide, and then warming and pressurizing; the fourth step is: out of the pot, putting it into the pot after leaving the pot. In the constant temperature scouring cylinder, soda ash and hydrogen peroxide are added to the constant temperature scouring cylinder, and the constant temperature scouring is carried out under normal pressure. The utility model has the beneficial effect that the silk sponge processed by the method can be washed, can not be hardened, has good fluffness and is comfortable.
【技术实现步骤摘要】
一种丝绵的加工方法
本专利技术涉及一种丝绵的制作工艺，特别涉及一种丝绵的加工方法。
技术介绍
现有市场上的丝绵及丝绵制品，其存在的缺陷是：不可水洗，容易板结，蓬松度差。
技术实现思路
针对现有丝绵质量和丝绵加工存在的缺点和不足，本专利技术提供了一种丝绵的加工方法。为了实现上述目的，本专利技术所采取的措施：一种丝绵的加工方法，第一步：将待加工的丝绵压紧装入高压高温的锅内；第二步：在锅内加入渗透剂和甲酸，然后加温加压；第三步：打开锅盖，加入甲基丙烯酰胺，再加温加压；第四步：出锅，出锅后放入到恒温煮练缸内，在恒温煮练缸内加入纯碱和双氧水，常压下恒温煮练；第五步：柔软，将恒温煮练好的丝绵放入到柔软缸内，加入柔软剂，搅拌；第六步：烘干，柔软后的丝绵出缸后，脱水、蒸汽烘干，完成丝绵的加工；所述的第二步中，丝绵、渗透剂和甲酸的重量比为500∶4∶7，加温加压后的温度为120℃，压力为4个标准大气压，加温加压的时间为2小时；所述的第三步中，加入的甲基丙烯酰胺与丝绵的重量比为8∶25，温度压力与第二步中相同，加温加压的时间为1.5小时；所述的第四步中，恒温煮练缸内放入的丝绵、纯碱和双氧...
【技术保护点】
1.一种丝绵的加工方法，其特征在于：第一步：将待加工的丝绵压紧装入高压高温的锅内；第二步：在锅内加入渗透剂和甲酸，然后加温加压；第三步：打开锅盖，加入甲基丙烯酰胺，再加温加压；第四步：出锅，出锅后放入到恒温煮练缸内，在恒温煮练缸内加入纯碱和双氧水，常压下恒温煮练；第五步：柔软，将恒温煮练好的丝绵放入到柔软缸内，加入柔软剂，搅拌；第六步：烘干，柔软后的丝绵出缸后，脱水、蒸汽烘干，完成丝绵的加工。
【技术特征摘要】
1.一种丝绵的加工方法，其特征在于：第一步：将待加工的丝绵压紧装入高压高温的锅内；第二步：在锅内加入渗透剂和甲酸，然后加温加压；第三步：打开锅盖，加入甲基丙烯酰胺，再加温加压；第四步：出锅，出锅后放入到恒温煮练缸内，在恒温煮练缸内加入纯碱和双氧水，常压下恒温煮练；第五步：柔软，将恒温煮练好的丝绵放入到柔软缸内，加入柔软剂，搅拌；第六步：烘干，柔软后的丝绵出缸后，脱水、蒸汽烘干，完成丝绵的加工。2.根据权利要求1所述的一种丝绵的加工方法，其特征在于：所述的第二步中，丝绵、渗透剂和甲酸的重量比为500∶4∶7，加温加压后的温...
【专利技术属性】
技术研发人员：张健健，
申请(专利权)人：杭州钱皇丝绸家纺有限公司，
类型：发明