竹塑复合板材配方组成比例

本发明专利技术公开了一种竹塑复合板材配方，包括竹塑发泡层、花纹层、UV涂层，其中竹塑发泡层配方质量份组成为：聚氯乙烯(PVC)树脂100份、竹粉30份、氯化聚乙烯(CPE)12份、钙锌复合稳定剂6份、聚酯增塑剂9份、硼酸酯偶联剂1.5份、AC发泡剂1.2份、碳酸氢钠0.8份、发泡调节剂3份、硬脂酸甘油脂0.3份、聚乙烯蜡0.8份。本发明专利技术能实现毛竹的规模化利用。

Formula of bamboo plastic composite plate

The invention discloses a bamboo-plastic composite plate formula, which comprises a bamboo-plastic foaming layer, a pattern layer and a UV coating. The formula of the bamboo-plastic foaming layer consists of 100 parts of polyvinyl chloride (PVC), 30 parts of bamboo powder, 12 parts of chlorinated polyethylene (CPE), 6 parts of calcium-zinc composite stabilizer, 9 parts of polyester plasticizer, 1.5 parts of borate coupling agent, AC. 1.2 phr of foaming agent, 0.8 phr of sodium bicarbonate, 3 phr of foaming regulator, 0.3 phr of glycerin stearate and 0.8 phr of polyethylene wax. The invention can realize large-scale utilization of Phyllostachys pubescens.

【技术实现步骤摘要】
竹塑复合板材配方
本专利技术涉及一种高分子复合材料配方，特别是一种竹塑复合板材配方。
技术介绍
PVC板材具有无甲醇、防腐蚀、重量轻、隔音、隔热等特点被广泛使用，大量毛竹未得到充分利用，将PVC、毛竹复合制成复合材料，能实现毛竹的规模化利用。
技术实现思路
本专利技术针对现有技术的不足，提出一种能实现毛竹的规模化利用的竹塑复合板材配方。本专利技术通过下述技术方案实现技术目标。竹塑复合板材配方，包括竹塑发泡层、花纹层、UV涂层，其改进之处在于：其中竹塑发泡层配方质量份组成为：聚氯乙烯(PVC)树脂100份、竹粉30份、氯化聚乙烯(CPE)12份、钙锌复合稳定剂6份、聚酯增塑剂9份、硼酸酯偶联剂1.5份、AC发泡剂1.2份、碳酸氢钠0.8份、发泡调节剂3份、硬脂酸甘油脂0.3份、聚乙烯蜡0.8份。本专利技术与现有技术相比，具有以下积极效果：1、将PVC、毛竹复合制成复合材料，能实现毛竹规模化利用。2、添加纳米活性碳酸钙，提高本专利技术的综合性能，而且减少制造成本。具体实施方式下面结合实施例对本专利技术作进一步说明。竹塑复合板材配方，包括竹塑发泡层、花纹层、UV涂层，其中竹塑发泡层配方质量份组成为：聚氯乙烯(PVC)树脂100份、竹粉30份、氯化聚乙烯(CPE)12份、钙锌复合稳定剂6份、聚酯增塑剂9份、硼酸酯偶联剂1.5份、AC发泡剂1.2份、碳酸氢钠0.8份、发泡调节剂3份、硬脂酸甘油脂0.3份、聚乙烯蜡0.8份。

【技术保护点】
1.一种竹塑复合板材配方，包括竹塑发泡层、花纹层、UV涂层，其特征在于：其中竹塑发泡层配方质量份组成为：聚氯乙烯(PVC) 树脂100份、竹粉30份、氯化聚乙烯(CPE)12份、钙锌复合稳定剂6份、聚酯增塑剂9份、硼酸酯偶联剂1.5份、AC 发泡剂1.2份、碳酸氢钠0.8份、发泡调节剂3份、硬脂酸甘油脂0.3份、聚乙烯蜡0.8份。

【技术特征摘要】
1.一种竹塑复合板材配方，包括竹塑发泡层、花纹层、UV涂层，其特征在于：其中竹塑发泡层配方质量份组成为：聚氯乙烯(PVC)树脂100份、竹粉30份、氯化聚乙烯(CP...

【专利技术属性】
技术研发人员：张冬平，
申请(专利权)人：张冬平，
类型：发明
国别省市：江苏,32