In order to solve the environmental pollution problem of the existing flame retardants and improve the quality of the existing polystyrene cement board, the present invention provides an inorganic flame retardant for the polystyrene cement-based insulation board, which is composed of the following raw materials: 40 to 60 parts by weight of ultra-fine calcium aluminate hydrate, 10 to 15 parts by weight of ultra-fine calcium hydroxide, 10 to 25 parts by weight of ultra-fine clouds. Mother, 1, 3, 1 coupling agents and 3 3 epoxy resins. Flame retardant can effectively prevent the delamination of cement paste by bonding it with polystyrene particles through epoxy resin, and improving the compatibility with cement paste by calcium aluminate hydrate, calcium hydroxide and coupling agent. The fire retardant grade of polystyrene particles with inorganic flame retardant can reach A2 grade.
【技术实现步骤摘要】
一种用于聚苯乙烯水泥基保温板的无机阻燃剂
本专利技术涉及阻燃剂
,尤其涉及用于聚苯乙烯水泥基保温板的阻燃剂,具体涉及一种用于聚苯乙烯水泥基保温板的无机阻燃剂。
技术介绍
可发性聚苯乙烯是在普通聚苯乙烯中浸渍低沸点的物理发泡剂加工过程中受热发泡制成的热塑性树脂,具有微细闭孔的结构特点,主要用于建筑墙体、屋面保温、复合板保温和冷库、空调、车辆、船舶的保温隔热。但是该材料属于易燃材料,存在引发火灾的安全隐患,并且在燃烧时火焰蔓延迅速,并伴有毒气和烟气产生,因此,需要进行防火阻燃改性。现在,一般添加溴系阻燃剂来改善聚苯乙烯的防火等级,但最高只能达到B1级,并且由于溴系阻燃剂破坏污染环境,在欧美国家已经禁止使用。尤其当聚苯乙烯用来制备水泥基保温板时,聚苯乙烯的憎水表面与水泥浆体的相容性差,在搅拌过程中易分层,而且与水泥硬化浆体粘结性差,影响聚苯乙烯水泥基保温板的品质。
技术实现思路
为解决现有阻燃剂的环境污染问题以及提高现有聚苯乙烯水泥基保温板的品质,本专利技术提供了一种用于聚苯乙烯水泥基保温板的无机阻燃剂。一种用于聚苯乙烯水泥基保温板的无机阻燃剂,由以下原料组成:重量份数40-60份超细水化铝酸钙、10-15份超细氢氧化钙、10-25份超细云母、1-3份偶联剂和1-3份环氧树脂载体。优选地,所用偶联剂为硬脂酸钙;优选地,所用水化铝酸钙的组成为C4AH13;优选地,所用环氧树脂载体为3%甲苯稀释的环氧树脂载体。优选地,一种用于聚苯乙烯水泥基保温板的无机阻燃剂,由以下原料组成:重量份数40份超细水化铝酸钙、10份超细氢氧化钙、25份超细云母、1份偶联剂和1份环氧树脂 ...
【技术保护点】
1.一种用于聚苯乙烯水泥基保温板的无机阻燃剂,其特征在于,由以下原料组成:重量份数40‑60份超细水化铝酸钙、10‑15份超细氢氧化钙、10‑25份超细云母、1‑3份偶联剂和1‑3份环氧树脂载体。
【技术特征摘要】
1.一种用于聚苯乙烯水泥基保温板的无机阻燃剂,其特征在于,由以下原料组成:重量份数40-60份超细水化铝酸钙、10-15份超细氢氧化钙、10-25份超细云母、1-3份偶联剂和1-3份环氧树脂载体。2.根据权利要求1所述的无机阻燃剂,其特征在于,所述的偶联剂...
【专利技术属性】
技术研发人员:宫晨琛,代文燕,芦令超,程新,
申请(专利权)人:济南大学,
类型:发明
国别省市:山东,37