一种新型尿醛呋喃树脂及其制备方法技术

本发明专利技术涉及一种新型尿醛呋喃树脂，按重量配比为：糠浆50‑100份、糠醇400‑500份、工业甲醛溶液400份、尿素100‑130份；其制备方法，包括如下步骤：首先将上述材料糠浆50‑100份、糠醇400‑500份、工业甲醛溶液400份、尿素100‑130份一次性投入反应斧中，反应斧升温加热，反应斧中溶液的PH值控制在8‑8.5，升温至75 ℃时保温30分钟，然后降温至60 ℃，调整PH值为5，又升温至85℃时反应1‑1.5小时，降温，加入少许尿素、硅脘、调整PH值为7‑7.5 出料即得到产品。

A new type of urea formaldehyde furan resin and its preparation method

The present invention relates to a new type of urea-formaldehyde-furan resin, which is proportioned by weight as follows: 50 100 furfural pulp, 400 500 furfural alcohol, 400 500 industrial formaldehyde solution and 100 130 urea. The preparation method includes the following steps: firstly, 50 100 fural pulp, 400 500 furfural alcohol, 400 Industrial formaldehyde solution and 100 1 urea. Thirty copies were put into the reaction axe at one time. The pH value of the solution in the reaction axe was controlled at 8 8.5, kept at 75 C for 30 minutes, then cooled to 60 C, adjusted to pH 5, and then raised to 85 C for 1.5 hours. The reaction temperature was lowered by adding a little urea, silica, and adjusted to pH 7 7.5. To the product.

【技术实现步骤摘要】
一种新型尿醛呋喃树脂及其制备方法
本专利技术涉及树脂材料制备
，具体涉及一种新型尿醛呋喃树脂及其制备方法。
技术介绍
尿醛呋喃树脂是广泛用于制造生产树脂自硬砂工艺中的合成树脂。由于其自身诸多优点（不复述）而逐年呈上升趋势。但目前市场应用的尿醛树脂存在以下几个缺陷：目前尿醛树脂中使用的尿醛价格居高不下，造成树脂自身成本很高，许多铸造企业难以接受。即使用也是在质量和成本之间艰难选择，造成铸造企业铸件质量趋下，生产成本上升的局面。由于糖醇成本高，企业在合成树脂时会大量使用成本低的尿素和甲醛，造成树脂因尿素增加含氮加大，树脂发气量加大，铸件气孔多，质量下降，另外甲醛加入量增高，树脂中游离甲醛增多，工人使用时造成对身体的危害和环境的污染。
技术实现思路
为了克服现有技术中存在的上述不足之处，本专利技术的目的在于提供一种新型尿醛呋喃树脂的制备方法，该制备方法即降低成本，提高产品质量，减少对工人身体危害和环境的污染。为实现上述目的，本专利技术采用的技术方案如下：一种新型尿醛呋喃树脂，按重量配比为：糠浆50-100份糠醇400-500份工业甲醛溶液400份尿素100-130份。上述一种新型尿醛呋喃本文档来自技高网...

【技术保护点】
1.一种新型尿醛呋喃树脂，其特征在于：按重量配比为：糠浆50‑100份糠醇400‑500份工业甲醛溶液400份尿素100‑130份。

【技术特征摘要】
1.一种新型尿醛呋喃树脂，其特征在于：按重量配比为：糠浆50-100份糠醇400-500份工业甲醛溶液400份尿素100-130份。2.根据权利要求1所述一种新型尿醛呋喃树脂的制备方法,其特征在于：包括如下步骤：首先将上述材料糠浆50-100份、糠醇400-500份、工业...

【专利技术属性】
技术研发人员：谢大英，
申请(专利权)人：晋江农发有机肥料制造有限公司，
类型：发明
国别省市：福建,35