The invention relates to cementitious materials, in particular to a method for preparing alpha high strength gypsum from waste gypsum molds, which mainly solves the problem of treating a large number of existing waste ceramic gypsum molds. Alpha high strength gypsum is prepared by using waste ceramic gypsum mold. It is characterized in that after crushing and grinding waste ceramic gypsum mold and adding a certain amount of water to prepare slurry, the dihydrate gypsum is transformed into alpha high strength gypsum by autoclaving process under the action of transcrystallizer. The invention handles the stacking of a large number of waste ceramic gypsum molds, protects the environment, realizes the comprehensive utilization of resources, has the advantages of simple process and good comprehensive performance of the prepared alpha high strength gypsum.
【技术实现步骤摘要】
一种用废石膏模制备α高强石膏的方法
本专利技术涉及一种α石膏的生产方法，尤其是涉及一种用废石膏模制备α高强石膏的方法。
技术介绍
随着近年来陶瓷行业的大力发展，废陶瓷石膏模等废料大量堆放。目前国内还未对石膏模进行合理有效的重复利用，大量废石膏模的堆放即占用大量的堆场，又污染环境，本专利技术利用废石膏模制备高强石膏能有效地解决此问题，还能形成一定的副价值。目前，针对α石膏的生产方法主要有三类，一是溶液法，将二水石膏磨细后加入常压加热或高压加热的装有转晶剂溶液的容器内，通过加热加压或常压加热的方式，在搅拌加热的方式下进行转晶，转晶后的物料经过滤、洗涤、烘干的生产方法；二是采用传统的蒸压法进行生产，天然石膏破碎筛分后将30-100mm的块状物料装入蒸压釜经蒸压后釜内或釜外烘干的方式；三是造粒法，主要是将粉状二水石膏与转晶剂溶液混合后成型或造粒，使其以块状或颗粒状送入蒸压设备进行转晶，然后再釜内或釜外烘干的方式。本专利技术在对蒸压法进行了改良，使制备的α高强石膏综合性能较好。
技术实现思路
本专利技术的目的，应用废陶瓷石膏模制备α高强石膏，其特征在于，废陶瓷石膏模在转晶剂的作...
【技术保护点】
1.一种用废石膏模制备α高强石膏的方法，其特征在于，包括以下步骤：a）将废石膏模磨碎成粉料，按0.4的水胶比加水搅拌成浆料；b）向步骤1制备的浆料中加入石膏质量的0.05%‑2.60%的转晶剂，搅拌均匀；c）将步骤2制备的浆料放入蒸压釜中，在0.2‑1.2MPa压力下蒸压，使二水石膏转化为α高强石膏；d）在60‑150℃下，烘干步骤3制备的α高强石膏至恒重；e）将步骤4制备的α高强石膏磨碎，过200目的筛。
【技术特征摘要】
1.一种用废石膏模制备α高强石膏的方法，其特征在于，包括以下步骤：a）将废石膏模磨碎成粉料，按0.4的水胶比加水搅拌成浆料；b）向步骤1制备的浆料中加入石膏质量的0.05%-2.60%的转晶剂，搅拌均匀；c）将步骤2制备的浆料放入蒸压釜中，在0.2-1.2MPa压力下蒸压，使二水石膏转化为α高强石膏；d）在60-150℃下，烘干步骤3制备的α高强石膏至恒重；e）将步骤4制备的α高强石膏磨碎，过200目的筛。2.按照权利要求1所述一种用废石膏模制备α高强石膏的方法，其特征在于：步骤1中的废石膏模为废陶瓷石膏模或其他废石膏模。3.按照权利要求1所述一种用废石膏模制备α高强石膏的方法，其...