The invention discloses a preparation method of PET plastic. When polybutylene terephthalate (PET) resin is used as the main resin, and coupling agent is added to the mixing machine according to the mixture, then the antioxidant, lubricant and nucleating agent are added in turn, the glass fiber is drawn in the side entrance of the extruder and finally squeezed out by the extruder to get the product. This method can be obtained. Improve the mechanical properties of products and improve the appearance and service life of the next stage products. The preparation method provided by the invention has the advantages of simple process, high yield and excellent lubrication, so as to protect the extruder equipment and has the functions of both internal and external consideration.
【技术实现步骤摘要】
一种PET塑料的制备方法
本专利技术涉及一种高分子材料
，尤其涉及一种PET塑料的制备方法。
技术介绍
聚对苯二甲酸乙二醇酯俗称涤纶树脂，学名为PET，由对苯二甲酸二甲酯与乙二醇酯交换或以对苯二甲酸与乙二醇酯化先合成对苯二甲酸双羟乙酯，然后再进行缩聚反应制得。增强PET是以PET树脂为基料，添加玻璃纤维亦或是添加其他纤维，经挤出机混炼挤出制得的塑料。用此方法生产所得的PET在一定程度上提高了树脂的强度和刚度，但是对某些要求超高强度的制件仍达不到要求。
技术实现思路
鉴于此，有必要提供一种强度高的PET塑料的制备方法。一种PET塑料的制备方法：按重量百分数，将48%~68%的PET与0.2%~0.6%的偶联剂,在混料机中混合，再依次加入0.2%~0.6%的抗氧剂、1%~3%的润滑剂、和0.2%~0.6%的成核剂，混合后得到第一混合物；将第一混合物与经挤出机侧入口牵引进入的比例为30%~50%的增强剂再进行混合，得到第二混合物；将第二混合物经挤出机挤出切粒，即得到本产品。所述PET为中等粘度的PET纯树脂。所述PET为有光的PET纯树脂。所述PET的特性粘度为0.6...
【技术保护点】
1.一种PET塑料的制备方法，其特征在于包括如下步骤： 按重量百分数，将48%~68%的PET与0.2%~0.6%的偶联剂，在混料机中混合，再依次加入0.2%~0.6%的抗氧剂、1%~3%的润滑剂、和0.2%~0.6%的成核剂，混合后得到第一混合物； 将第一混合物与经挤出机侧入口牵引进入的比例为30%~50%的增强剂再进行混合，得到第二混合物； 将第二混合物经挤出机挤出切粒。
【技术特征摘要】
1.一种PET塑料的制备方法，其特征在于包括如下步骤：按重量百分数，将48%~68%的PET与0.2%~0.6%的偶联剂，在混料机中混合，再依次加入0.2%~0.6%的抗氧剂、1%~3%的润滑剂、和0.2%~0.6%的成核剂，混合后得到第一混合物；将第一混合物与经挤出机侧入口牵引进入的比例为30%~50%的增强剂再进行混合，得到第二混合物；将第二混合物经挤出机挤出切粒。2.根据权利要求1所述PET塑料的制备方法，其特征在于：所述PET为中等粘度的PET纯树脂。3.根据权利要求1所述PET塑料的制备方法，其特征在于：所述PET为有光的PET纯树脂。4.根据权利要求1所述PET塑料的制备方法，其特征在于：所述PET的特性粘度为0.65~0.68分升/克。5.根据权利要求1所述PET塑料的制备方法，其特征在于：所述增强剂为玻璃纤维...