The invention relates to the technical field of building thermal insulation materials, in particular to a high-performance inorganic thermal insulation mortar and a preparation method thereof. The thermal insulation mortar consists of the following raw materials: 100~120 common portland cement, 40~50 vitrified microspheres, 0.3 to 0.5 cellulose ether, 1~2 dispersible latex powder, 1~3 phr silica aerogels, 0.3 to 0.6 polypropylene fibers, 1~3 parts of silicone water repellent, 0.5 to 1 water reducer, 0.5 ~ 1.5 dilatant waterproofing agents. 120~140 copies of water. The high performance inorganic insulation mortar has good compressive strength, low thermal conductivity and water absorption.
【技术实现步骤摘要】
一种高性能无机保温砂浆及其制备方法
本专利技术涉及一种高性能无机保温砂浆及其的制备方法，属于建筑保温材料领域。
技术介绍
随着建筑节能大力推广，建筑节能材料品种繁多。每种保温材料都有各自的优缺点。无机保温砂浆阻燃性好，线性膨胀系数与建筑本身一致，但其保温性没有有机材料好，同时吸水率也大。无机保温砂浆吸水率、导热系数、表观密度及强度这四个性能之间有着相反相容的关系，当表观密度越低时，导热系数越小，抗压强度越低，内部空隙增多，吸水率越大。因此保证抗压强度的同时，降低其导热系数和吸水率是高性能无机保温砂浆追求目标。
技术实现思路
本专利技术的目的在于提供一种高性能无机保温砂浆制备方法，该高性能保温砂浆在保证强度和表观密度的同时，又具有较低的导热系数及吸水率。本专利技术的技术方案如下：一种高性能无机保温砂浆，由下列重量份的原材料制备而成：普通硅酸盐水泥100～120份、玻化微珠40～50份、纤维素醚0.3～0.5份、可分散性乳胶粉1～2份、二氧化硅气凝胶1～3份、聚丙烯纤维0.3～0.6份、有机硅憎水剂1～3份、减水剂0.5～1份、膨胀防水剂0.5～1.5份，水120～140...
【技术保护点】
1.一种高性能无机保温砂浆，其特征在于，由下列重量份的原材料制备而成：普通硅酸盐水泥100～120份、玻化微珠40～50份、纤维素醚0.3～0.5份、可分散性乳胶粉1～2份、二氧化硅气凝胶1～3份、聚丙烯纤维0.3～0.6份、有机硅憎水剂1～3份、减水剂0.5～1份、膨胀防水剂0.5～1.5份，水120～140份。
【技术特征摘要】
1.一种高性能无机保温砂浆，其特征在于，由下列重量份的原材料制备而成：普通硅酸盐水泥100～120份、玻化微珠40～50份、纤维素醚0.3～0.5份、可分散性乳胶粉1～2份、二氧化硅气凝胶1～3份、聚丙烯纤维0.3～0.6份、有机硅憎水剂1～3份、减水剂0.5～1份、膨胀防水剂0.5～1.5份，水120～140份。2.根据权利要求1所述的高性能无机保温砂浆，其特征在于：所述普通硅酸盐水泥为42.5普通硅酸盐水泥。3.根据权利要求1所述的高性能无机保温砂浆，其特征在于：所述玻化微珠堆积密度为100～120kg/m3。4.根据权利要求1所述的高性能无机...