本发明专利技术涉及金属加工技术领域，尤其是一种以锰、铬、硅和生铁生产白口铸铁的方法，其化学成分百分比为：锰9％‑11％，铬5％‑8％，硅3％‑5％，余量为生铁；以锰、铬、硅、生铁、废钢等普通材料通过特定配比制成白口铸铁，铸铁组织全部发生白口化，加工过程中无需经过高频热处理，具有表面强度高，内外硬度一致等优点；适合生产活塞、活塞杆和柱塞等用于长期摩擦的部件。

A method for producing white cast iron from manganese, chromium, silicon and pig iron

The invention relates to the field of metal processing technology, in particular a method of producing white cast iron with manganese, chromium, silicon and pig iron. The percentage of the chemical composition is manganese 9%, chromium 5%, 8%, 3% silicon and 5%, and the residual amount is pig iron; it is made of manganese, chromium, silicon, pig iron, scrap and other ordinary materials to make white casting through a specific ratio. Iron and cast iron are all whitening, without high frequency heat treatment, with high surface strength and uniform internal and external hardness. It is suitable for the production of piston, piston rod and plunger for long friction parts.

【技术实现步骤摘要】
一种以锰、铬、硅和生铁生产白口铸铁的方法
本专利技术涉及金属加工
，尤其是一种以锰、铬、硅和生铁生产白口铸铁的方法。
技术介绍
铸铁其外观一般为铁黑色或者灰色，在铸造成产品后需要打磨后喷涂亮色涂料，然而对于活塞杆、柱塞等由于经常摩擦，并不适合喷涂涂料。故急需一种铸造后天然呈现白口状态的铸铁。
技术实现思路
针对现有技术的不足，本专利技术提供一种白口铸铁的生产方法。本专利技术的技术方案为：一种以锰、铬、硅和生铁生产白口铸铁的方法，其特征在于：其化学成分百分比为：锰9％-11％，铬5％-8％，硅3％-5％，余量为生铁。一种以锰、铬、硅和生铁生产白口铸铁的方法，其具体步骤如下：以重量百分比计，将锰9％-11％，铬5％-8％，硅3％-5％，余量为生铁进行配料；将生铁放入感应炉内熔化后，进行预脱氧操作，而后加入铬铁、锰铁和硅铁，得到铁水；取铁水试样进行炉前分析，根据分析结果，将所述铁水调整至合格铁水的要求；将铁水温度提高到1550℃～1600℃，进行终脱氧，出炉；待温度降至1400℃～1460℃时，开始浇注，得铸铁；将获得的铸铁加热到850℃～950℃，进行空冷，然后加热到350℃～500℃本文档来自技高网...

【技术保护点】
1.一种以锰、铬、硅和生铁生产白口铸铁的方法，其特征在于：其化学成分百分比为：锰9％‑11％，铬5％‑8％，硅3％‑5％，余量为生铁。

【技术特征摘要】
1.一种以锰、铬、硅和生铁生产白口铸铁的方法，其特征在于：其化学成分百分比为：锰9％-11％，铬5％-8％，硅3％-5％，余量为生铁。2.根据权利要求1所述的一种以锰、铬、硅和生铁生产白口铸铁的方法，其特征在于：其化学成分百分比为：锰9％，铬5％，硅3％，余量为生铁。3.根据权利要求1所述的一种以锰、铬、硅和生铁生产白口铸铁的方法，其特征在于：其化学成分百分比为：锰11％，铬8％，硅5％，余量为生铁。4.根据权利要求1所述的一种以锰、铬、硅和生铁生产白口铸铁的方法，其特征在于：其化学成分百分比为：10％，铬6％，硅4％，余量为生铁。5.根据权利要求1所述的一种以锰、铬、硅和生铁生产白口铸铁的方法，其...

【专利技术属性】
技术研发人员：林星国，林星华，林松花，林浩，
申请(专利权)人：四会市楠铧机械有限公司，
类型：发明
国别省市：广东,44