紫金釉及其烧制方法技术

一种紫金釉，通过龙泉原白釉、紫金土、高岭土、龙泉市铥矿原石配比制成，再通过原料混合、施釉、烧制制成。本发明专利技术有益的效果是：采用紫金釉烧制出来的紫金铁胎杯，泡茶时能够使茶水酸性降低，使茶水喝起来口感鲜爽、清甜，提高茶水的口感，同时能够使茶水中的矿物元素增多，利于人体吸收，起到了保健的功能，起到了养生的功效，健康环保，这是市面上常规瓷器所无法达到的效果。

Purple Gold glaze and its burning method

A purple gold glaze is made from the raw white glaze of Longquan, purple gold, kaolin, and Longquan thulium ore. It is made by mixing raw materials, glazing and firing. The beneficial effect of the invention is that the purple gold iron cup is made by the purple gold glaze, which can reduce the acidity of the tea water, make the tea drink taste fresh and sweet, improve the taste of the tea water, increase the mineral elements in the tea water, be beneficial to the body and play a health care function and raise the health. Efficacy, health and environmental protection, this is the effect of conventional porcelain on the market.

【技术实现步骤摘要】
紫金釉及其烧制方法
本专利技术涉及青瓷制作
，尤其涉及一种紫金釉及其烧制方法。
技术介绍
釉是覆盖在瓷器制品表面的无色或有色的玻璃质薄层，是用矿物原料(长石、石英、滑石、高岭土等)按一定比例配合经过研磨制成釉浆，施于坯体表面，经一定温度煅烧而成。能增加制品的机械强度、热稳定性和电介强度，还有美化器物、便于拭洗、不被尘土腥秽侵蚀等特点。青瓷常作为泡茶的瓷器，而喝茶已成为人们生活当中重要的一部分了，对于喝茶，口感是第一位，其次是茶水所带来的养生效果，而市面上的常规瓷器仅具有盛放茶水的功能，已经无法满足人们的需求了。
技术实现思路
本专利技术要解决上述现有技术存在的问题，提供一种紫金釉及其烧制方法，采用紫金釉烧制的茶杯，泡茶时茶水酸性降低，提高了茶水的口感，并具有养生功能，满足人们的需求。本专利技术解决其技术问题采用的技术方案：这种紫金釉，它是由下列重量份的原料配比制成：龙泉原白釉30份～40份、紫金土24份～26份、高岭土9份～11份、龙泉市铥矿原石28份～35份。进一步的，它是由下列重量份的原料配比制成：龙泉原白釉35份、紫金土25份、高岭土10份、龙泉市铥矿原石30份。上述的紫金釉本文档来自技高网...

【技术保护点】
1.一种紫金釉，其特征在于，它是由下列重量份的原料配比制成：龙泉原白釉30份～40份、紫金土24份～26份、高岭土9份～11份、龙泉市铥矿原石28份～35份。

【技术特征摘要】
1.一种紫金釉，其特征在于，它是由下列重量份的原料配比制成：龙泉原白釉30份～40份、紫金土24份～26份、高岭土9份～11份、龙泉市铥矿原石28份～35份。2.根据权利要求1所述的紫金釉，其特征在于，它是由下列重量份的原料配比制成：龙泉原白釉35份、紫金土25份、高岭土10份、龙泉市铥矿原石30份。3.根据权利要求1或2所述的紫金釉的烧制方法是：(1)原料混合，将选取的龙泉原白釉、紫金土、高岭土、龙泉市铥矿原石进行均匀混合，湿法球磨70小时，然后将球磨后的原料过220目～240目筛，得到釉料；(2)施釉，将获得的釉料加水调制成56～64波美度的釉浆，然后取瓷器素胚，采用浸釉法对素胚施釉，施釉完毕后置于阴凉通风处进行自然风干，干燥时间为14小...

【专利技术属性】
技术研发人员：黄俊龙，
申请(专利权)人：黄俊龙，
类型：发明
国别省市：浙江,33