The invention discloses a new synthetic leather material. According to the weight number, it consists of 50 parts, 20 bamboo powder, 20 bamboo powder, 30 parts, 8 thermoplastic resin powder, 15 radish skin 30 and 5 shellac, 5 copies. The invention also discloses a preparation method of the new synthetic leather material. The prepared raw material used in the invention has no polyurethane resin, and avoids the use of toxic chemical solvents such as N, N 'two methyl formamide and toluene. The preparation process of synthetic leather is safe and pollution-free; the synthetic leather is soft and resilient, has strong wear resistance, and also has heat resistance. Light resistance, water resistance, resistance to methanol and other chemical solvents, good permeability.
【技术实现步骤摘要】
一种新型合成革材料及其制备方法
本专利技术涉及一种新型合成革材料及其制备方法。
技术介绍
目前，合成革的生产工艺主要有湿法和干法两种，不论是使用干法聚氨酯制革工艺还是湿法聚氨酯制革工艺，在合成革生产过程中，都需要使用大量有毒害的有机溶剂，如N,N’-二甲基甲酰胺、丙酮、甲苯等。市面上绝大多数的合成革，都以聚氨酯树脂为主要材料，而如前所述，聚氨酯树脂，不仅在生产过程中需要用到有毒溶剂，其本身也含有不易挥发的有机物，因此制造出的合成革通常有较大异味，处理不当可能对人体造成伤害，并且，聚氨酯树脂本身不易降解，其制备过程中所用到的有毒有害的有机溶剂，需要大量的后续工作来处理，否则会对环境造成很大危害，这也就是目前合成革行业不环保的主要原因，也是限制合成革制造业发展的一个重要因素。
技术实现思路
本专利技术为了克服现有技术的不足，提供一种新型合成革材料及其制备方法。为了实现上述目的，本专利技术采用以下技术方案：一种新型合成革材料，按照重量份数计，由以下成份组成：麻丝40-50份，竹粉20-30份，热塑性树脂粉8-15份，萝卜皮15-30份，虫胶1-5份。作为优选，所述萝卜皮为白...
【技术保护点】
1.一种新型合成革材料，其特征是，按照重量份数计，由以下成份组成：麻丝40‑50份，竹粉20‑30份，热塑性树脂粉8‑15份，萝卜皮15‑30份，虫胶1‑5份。
【技术特征摘要】
1.一种新型合成革材料，其特征是，按照重量份数计，由以下成份组成：麻丝40-50份，竹粉20-30份，热塑性树脂粉8-15份，萝卜皮15-30份，虫胶1-5份。2.根据权利要求1所述的新型合成革材料，其特征是，按照重量份数计，由以下成份组成：麻丝42份，竹粉26份，热塑性树脂粉11份，萝卜皮25份，虫胶5份。3.根据权利要求1所述的新型合成革材料，其特征是，按照重量份数计，由以下成份组成：麻丝45份，竹粉28份，热塑性树脂粉9份，萝卜皮21份，虫胶3份。4.根据权利要求1所述的新型合成革材料，其特征是，萝卜皮采用白萝卜皮。5.根据权利要求1所述的新型合成革材料，其特征是，该合成革包括基层和面层，其中，按重量份数计，基层由以下成分组成：麻丝25-30份，竹粉10-15份，虫胶1-3份，面层由以下成分组成：麻丝15-20份，竹粉10-15份，热塑性树脂粉8-15份，萝卜皮15-30份，虫胶1-2份。6.一种新型合成革材料的制备方法，其特征是，该方法用于制备权利要求1-5中任一项所述的新型合成革材料，并包括以下步骤：(1)备料...
【专利技术属性】
技术研发人员：邵烨，黄胜乾，夏怀波，
申请(专利权)人：浙江闽锋化学有限公司，
类型：发明
国别省市：浙江,33