一种耐光红色分散染料组合物制造技术

本发明专利技术公开一种耐光红色分散染料组合物制备的方法，属于纺织化工技术领域。该染料由以下组分组成:重量分数为50‑92％的分散红56染料，重量分数为5‑45％的分散红126染料，重量分数为1‑10％的分散红79染料，其余为助剂。该分散染料能够用在聚酯纤维汽车内饰织物等产品的染色上，使用本染料可以最大限度的降低由于日光照射而导致的织物变褪色的现象，从而使染色织物日晒牢度大大提高，且染色均染性好、其他各项色牢度都达到最佳。

A light resistant red disperse dye composition

The invention discloses a method for preparing a light resistant red disperse dye composition, which belongs to the technical field of textile and chemical industry. The dyestuff consists of the following components: a disperse red 56 dye with a weight fraction of 50 and 92%, a disperse red 126 dye with a weight fraction of 45%, and a disperse red 79 dye with a weight fraction of 1 10%, and the other as an auxiliary. The disperse dye can be used in dyeing of polyester fiber automobile interior fabric and other products. Using this dye can minimize the fading of fabric caused by sunlight, so that the color fastness of dyed fabric is greatly improved, and the dyeing property is good and its color fastness is best.

【技术实现步骤摘要】
一种耐光红色分散染料组合物
本专利技术涉及一种耐光红色分散染料组合物制备的方法，属于纺织化工

技术介绍
目前，针对户外运动的增加，汽车销量的增长，各种汽车配套内饰织物产品的品种越来越多，而这些物品通常是在高温下暴露于日光，容易发生颜色的褪变，并难以保证在很长一段时间内保持良好的颜色，因此对日晒牢度的要求也越来越高，如何降低日光照射后织物的变褪色成为重点研究的课题。因此，作为对上述情况的理解，必须使用具有特别好耐光牢度的染料对户外用品所用的聚酷纤维进行染色，但是过去很少有耐光牢度特别好的红色分散染料来染汽车内饰等这些织物。现市场急需要用于聚酯纤维高耐光牢度的分散染料产品来满足日益增长的消费需求。
技术实现思路
针对现有技术的不足，本专利技术的主要目的在于提供一种耐光红色分散染料组合物制备的方法。为实现前述专利技术目的，本专利技术采取的技术方案如下：一种耐光红色分散染料组合物，其特征在于该染料由下列组分组成：重量分数为64-90％的分散红56染料，重量分数为5-35％的分散红126染料，重量分数为1-5％的分散红79染料，其余为助剂。所述的一种耐光红色分散染料组合物，其特征在于：所本文档来自技高网...

【技术保护点】
1.一种耐光红色分散染料组合物，其特征在于该染料由下列组分组成：重量分数为64‑90％的分散红56染料，重量分数为5‑35％的分散红126染料，重量分数为1‑5％的分散红79染料，其余为助剂。

【技术特征摘要】
1.一种耐光红色分散染料组合物，其特征在于该染料由下列组分组成：重量分数为64-90％的分散红56染料，重量分数为5-35％的分散红126染料，重量分数为1-5％的分散红79染料，其余为助剂。2.根据权利要求1所述的一种耐光红色分散染料组合物，其特征在于：所述的红色染料与助剂的重量分数比为1～3.5:1。3.根据权利要求1所述的一种耐光红色分散染料组合物...

【专利技术属性】
技术研发人员：卜广玖，王震，李柏毅，陆前进，汪娇，殷允杰，
申请(专利权)人：菲诺染料化工无锡有限公司，江南大学，
类型：发明
国别省市：江苏,32