The invention discloses an integral foam ceiling which is not easily deformed. It consists of the following raw materials: 80 chlorinated polyethylene, 84 parts, methyl triethoxy silane 7, 130 water, 4.5 light calcium talcum 4.5, 0.8 peroxide, two cumene, 0.8, 1.2, 7 stabilizers and second uncle Ding Ji There are 0.5 copies of cresol 0.3, 12 vitrified beads and 0.4 water reducing agent, and 0.8 water reducing agent 0.4. The invention has good insulation and sound absorption effect, and has no deformation and cracking phenomenon for a long time, and the whole installation is convenient. One
【技术实现步骤摘要】
一种不易变形整体式泡沫天花板
本专利技术涉及天花板领域,具体属于不易变形整体式泡沫天花板。
技术介绍
天花板吊顶材料需要具备阻燃、隔热、吸音等性能,还需要具备自身重量小,安装方便等性能。目前,市场上的发泡天花板存在着隔热吸音效果差,且长时间使用容易出现变形开裂的现象,且安装不方便等缺点。
技术实现思路
本专利技术的目的是提供一种不易变形整体式泡沫天花板,具有较好的隔热吸音效果,且长时间使用不出现变形开裂的现象,且整体安装方便。为了解决上述技术问题,本专利技术采用的技术方案如下:一种不易变形整体式泡沫天花板,由以下重量份的原料组成:氯化聚乙烯80-84份、甲基三乙氧基硅烷7-8份、水120-130份、轻钙滑石粉4.5-5.5份、过氧化二异丙苯交联剂0.8-1.2份、稳定剂0.3-0.5份、2,6-二叔丁基对甲酚0.3-0.5份、玻化微珠10-12份、减水剂0.4-0.8份;该天花板的具体制备方法是在高压釜中于85-90℃将氯化聚乙烯软化,压力保持在0.8-1MPa,备用;再将轻钙滑石粉均匀分散于水中制得溶液,该溶液与甲基三乙氧基硅烷一同加入到高压釜内与软化后的氯化聚乙烯充分混合,冷却到常温后,得到预发泡料,预发泡料再与剩余所有原料均匀混合后,放入天花板成型模具中加热成型,模具的温度为150-210℃,冷却后即为泡沫天花板。一种不易变形整体式泡沫天花板,由以下重量份的原料组成:氯化聚乙烯80份、甲基三乙氧基硅烷7份、水120份、轻钙滑石粉4.5份、过氧化二异丙苯交联剂0.8份、稳定剂0.3份、2,6-二叔丁基对甲酚0.3份、玻化微珠10份、减水剂0.4份。一种不易 ...
【技术保护点】
1.一种不易变形整体式泡沫天花板,其特征在于,由以下重量份的原料组成:氯化聚乙
【技术特征摘要】
1.一种不易变形整体式泡沫天花板,其特征在于,由以下重量份的原料组成:氯化聚乙烯80-84份、甲基三乙氧基硅烷7-8份、水120-130份、轻钙滑石粉4.5-5.5份、过氧化二异丙苯交联剂0.8-1.2份、稳定剂0.3-0.5份、2,6-二叔丁基对甲酚0.3-0.5份、玻化微珠10-12份、减水剂0.4-0.8份;该天花板的具体制备方法是在高压釜中于85-90℃将氯化聚乙烯软化,压力保持在0.8-1MPa,备用;再将轻钙滑石粉均匀分散于水中制得溶液,该溶液与甲基三乙氧基硅烷一同加入到高压釜内与软化后的氯化聚乙烯充分混合,冷却到常温后,得到预发泡料,预发泡料再与剩余所有原料均匀混合后,放入天花板成...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。