A new method of high performance sealing material die pressing is characterized by including the following steps: Step 1, the soft PVC material is injected into the vacuum plastic mold through a extruder, and the plastic suction temperature is controlled between 90 and 110 degrees; step two, the plastic is completed, and the PVC soft plastic is put in a vacuum cooling setting; step three, cooling out. PVC soft plastic stripping. The soft PVC material is made of lead-free rubber. The advantages of the invention: the new method of high performance sealing material compression molding, by changing the PVC hard insulating material into PVC soft insulating material, reduces the processing temperature requirement, simplifies the production process, and makes the insulation and sealing performance of the material greatly improved and full use requirements. One
【技术实现步骤摘要】
一种高性能密封材料压模新方法
本专利技术涉及一种特殊形成加工工艺，特别提供了一种高性能密封材料压模新方法。
技术介绍
现在，很多工业生产中都需要采用密封材料，例如，卡槽组合式空调箱体内用于密封和强度定型的卡槽铝型材，密封需要用软材质，而强度定型则需要用硬材质，还有做法是把软硬两种材料分开吸塑成型，成型后再把两种材料组合成一体，但是，现在的密封材料加工工艺较为复杂，投入成本较高，技术还有待于改进和发展。
技术实现思路
本专利技术的目的是为了解决上述存在的诸多技术问题，特提供了一种高性能密封材料压模新方法。本专利技术提供了一种高性能密封材料压模新方法，其特征在于，包括以下步骤：步骤一，将软质PVC材料通过挤塑机注入真空吸塑模具中，同时控制吸塑温度在90-110度之间；步骤二，吸塑完成，把PVC软质塑料进行真空冷却定型；步骤三，冷却完成，PVC软质塑料脱模。所述的所述软质PVC材料为无铅橡胶材质。本专利技术的优点：本专利技术所述的高性能密封材料压模新方法，通过将PVC硬质绝缘材料改成PVC软质绝缘材料，降低了加工温度要求，简化了生产工艺，同时使得材料的绝缘性和密封性能大大提高，满足使用要求。具体实施方式实施例1本实施例提供了一种高性能密封材料压模新方法，其特征在于，包括以下步骤：步骤一，将软质PVC材料通过挤塑机注入真空吸塑模具中，同时控制吸塑温度在90-110度之间；步骤二，吸塑完成，把PVC软质塑料进行真空冷却定型；步骤三，冷却完成，PVC软质塑料脱模。所述的所述软质PVC材料为无铅橡胶材质。
【技术保护点】
1.一种高性能密封材料压模新方法，其特征在于，包括以下步骤 ：
【技术特征摘要】
1.一种高性能密封材料压模新方法，其特征在于，包括以下步骤：步骤一，将软质PVC材料通过挤塑机注入真空吸塑模具中，同时控制吸塑温度在90-110度之间；步骤二，吸塑完成，把...