The present invention relates to an improved cement, including cement, cementing sand, water reducing agent, water, and cement. The ratio of the cement to water is 1:0.83, the ratio of the cement to water is 1:0.3 0.34, and the proportion of the cement and water reducing agent is 1:0.08 0.01. By setting up the improved cement, the cement hardening time is shortened, the production efficiency is improved, the formula is shortened to 1 2 hours, the water cement ratio is reduced, the amount of water reducing agent is increased, and the drying time of cement is reduced.
【技术实现步骤摘要】
一种改进的水泥
本专利技术涉及一种改进的水泥。
技术介绍
现有的水泥强度较低,水泥胶装时,水泥浆容易流出,导致法兰和瓷件污染严重,清理难度加大。由于目前客户要求瓷套强度大,若按照目前的配比,裕度不是很大。胶装员工反馈目前的水泥配方容易造成水泥浆外流,导致增加无谓的法兰和瓷件清理时间。现有配方,水泥表干时间过长,需要3-4小时。
技术实现思路
为了克服现有技术的不足,本专利技术提供了一种改进的水泥。为解决上述问题,本专利技术所采用的技术方案是:一种改进的水泥,包括水泥,胶装砂,减水剂,水,所述的水泥,胶装砂的比例为1:0.83,所述的水泥与水的比例为1:0.3-0.34,所述的水泥与减水剂的比例为1:0.08-0.01。作为一种优选,所述的水为洁净淡水。作为一种优选,所述的胶装砂为110目。作为一种优选,所述的水泥与减水剂的比例为1:0.09。作为一种优选,所述的水泥与水的比例为1:0.32。作为一种优选,所述的水泥由硅酸盐水泥熟料、5%-20%的混合材料及适量石膏磨细制成。作为一种优选,所述的减水剂为水剂减水剂。由于采用了上述技术方案,与现有技术相比,本专利技术通过改进的水泥的设置,水泥硬化时间缩短,提高生产效率,配方缩短为1-2小时,减少水灰比,增加减水剂用量,减少水泥表干时间。同时下面结合具体实施方式对本专利技术作进一步说明。具体实施方式实施例:一种改进的水泥,包括水泥,胶装砂,减水剂,水,所述的水泥,胶装砂的比例为1:0.83,所述的水泥与水的比例为1:0.3-0.34,所述的水泥与减水剂的比例为1:0.08-0.01。进一步的,所述的水为洁净淡水。进一 ...
【技术保护点】
一种改进的水泥,包括水泥,胶装砂,减水剂,水,所述的水泥,胶装砂的比例为1:0.83,所述的水泥与水的比例为1:0.3‑0.34,所述的水泥与减水剂的比例为1:0.08‑0.01。
【技术特征摘要】
1.一种改进的水泥,包括水泥,胶装砂,减水剂,水,所述的水泥,胶装砂的比例为1:0.83,所述的水泥与水的比例为1:0.3-0.34,所述的水泥与减水剂的比例为1:0.08-0.01。2.如权利要求1所述的改进的水泥,其特征在于:所述的水为洁净淡水。3.如权利要求1所述的改进的水泥,其特征在于:所述的胶装砂为110目。4.如权利要求1所...
【专利技术属性】
技术研发人员:杨道辉,周波,
申请(专利权)人:湖南省醴陵市浦口华高电瓷电器有限公司,
类型:发明
国别省市:湖南,43
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。