The invention relates to a preparation method of polymeric zirconium chloride aluminum inorganic high efficient flocculant, which belongs to the technical field of water treatment. The invention is aimed at the poor ability of inorganic low molecular zirconium salt flocculant to adapt to the pH value of raw water. By prehydrolysis of aluminum salt and zirconium salt at the same time, the hydrolysate of aluminum salt formed after copolymerization can widen the wide range of pH value of the original water, and the size of the hydrolysate of zirconium salt can greatly enhance the organic pollutants in water. Efficient removal. The invention is especially suitable for enhanced coagulation treatment of raw water with high pH content and non neutral high organic content.
【技术实现步骤摘要】
一种聚合氯化锆铝无机高效絮凝剂的制备方法
本专利技术属给水处理领域，特别涉及一种聚合氯化锆铝无机高效絮凝剂的制备方法。
技术介绍
混凝是给水处理工艺中的重要单元，其对污染物的去除效果直接决定着后续工艺的运行负荷及最终出水水质。有研究表明，混凝单元对有机物的去除效果与后续加氯消毒步骤中生成的消毒副产物的多少呈正比关系。即有机物去除效果佳，消毒副产物的生成量少。这些消毒副产物已被证实可致癌，其形成应予以最大限度地限制。为此，如何提高混凝单元对有机物的去除效能受到业内的广泛关注，并成为综合优化混凝效果的重要目标之一。铝盐絮凝剂在过去的近百年的工程应用中发挥了重要作用。而其对有机物的去除效果有限，尤其是对小分子有机物的去除效果不佳。为了提高有机物的去除效果，增加铝盐絮凝剂的投加量是常用手段。而这一操作会使得出水中的残余铝含量增加，长期饮用高铝含量的水不利于人体健康，并会增加患心脑疾病的风险。为此，研制新型絮凝剂以提高有机物(特别是小分子有机物)的去除效果是当前研究的热点问题。无机低分子锆盐絮凝剂可实现对有机物的高效去除，特别是相比于铝盐絮凝剂对小分子有机物的去除效果有显著...
【技术保护点】
一种聚合氯化锆铝无机高效絮凝剂的制备方法，其特征在于：所用原料：氯化铝；四氯化锆和氢氧化钠；其制备步骤如下：(1)称取原料，配制溶液；(2)将四氯化锆溶液与氯化铝溶液按照Zr/Al摩尔比为2～5：1进行复配并充分混合；(3)将氢氧化钠溶液逐滴加入到步骤(2)中的复配混合液中，调节碱化度B为0.5～2.0，碱化度B是指[OH]/[Zr+Al]的摩尔比值；室温20～25℃下以500～600rpm持续搅拌至溶液呈无色透明后，静置熟化10～12小时，得到聚合氯化锆铝溶液。
【技术特征摘要】
1.一种聚合氯化锆铝无机高效絮凝剂的制备方法，其特征在于：所用原料：氯化铝；四氯化锆和氢氧化钠；其制备步骤如下：(1)称取原料，配制溶液；(2)将四氯化锆溶液与氯化铝溶液按照Zr/Al摩尔比为2～5：1进行复配并充分混合；(3)将氢氧化钠溶液逐滴加入到步骤(2)中的复配混合液中，调节碱化度B为0.5～2.0，碱化度B是指[OH]/[Zr+Al]的摩尔比值；室温20～25℃下以500～600rpm持续搅拌至溶液呈无色透明后，静置熟化10～12小时，得到聚合氯化锆铝...
【专利技术属性】
技术研发人员：李星，苏兆阳，杨艳玲，杜鹏，
申请(专利权)人：北京工业大学，
类型：发明
国别省市：北京,11
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。