The invention provides a nano ceramic coating for high temperature resistance at 800 C. The nano ceramic coating consists of the following raw materials with a number of weight parts: siloxane: 32, 40 copies, 12~22 copies of polyvinyl butyral fluid, 10 inorganic pigments, 18 copies of inorganic pigments, 16 stuffing 32, 0.5 1.4 copies, 0.2 dispersants: 1, dissolution Agent: 3, 6 copies. The nano ceramic coating used for high temperature resistance at 800 C is a single component coating, which does not need the complex rolling and ripening process of the traditional ceramic coating, and can ensure the integrity of the coating performance.
【技术实现步骤摘要】
耐800℃高温用纳米陶瓷涂料及其制备工艺
本专利技术涉及涂料
，具体涉及一种耐800℃高温用纳米陶瓷涂料，同时，本专利技术还涉及该涂料的制备工艺。
技术介绍
随着现代科学技术的发展，许多工业(如：石油石化、天然气、冶金、矿山等工业高温冶炼窑炉、炉膛、回转窑、热交换器、排烟管道等设备外表面防护)在高温环境作业的要求越来越高，对耐高温防护涂层的性能要求也越来越苛刻。目前，市面上主要使用为有机硅耐高温涂料，含有大量的有机挥发性化合物(VOC)，对于环境有着极大的危害，且有机硅涂料耐高温涂料在600℃时开始分解碳化，高温下易燃烧冒烟，产生有毒气体。无机纳米陶瓷涂料由于其具有绿色健康环保的特性，并且高温下不燃烧、不冒烟，无有毒气体释放，同时可满足耐瞬间高温的性能，近几年已逐渐开始在高温行业应用。
技术实现思路
本专利技术提供一种耐800℃高温用纳米陶瓷涂料，可常温自固化，解决了陶瓷涂料需高温烘烤固化的难题。一种耐800℃高温用纳米陶瓷涂料，由以下重量份数的原材料组成：硅氧烷：32-40份聚乙烯醇缩丁醛液：12～22份无机颜料：10-18份填料：16-32份分散剂：0.5-...
【技术保护点】
一种耐800℃高温用纳米陶瓷涂料，其特征在于，所述纳米陶瓷涂料由以下重量份数的原材料组成：硅氧烷：32‑40份聚乙烯醇缩丁醛液：12～22份无机颜料：10‑18份填料：16‑32份分散剂：0.5‑1.4份流平剂：0.2‑1份溶剂：3‑6份。
【技术特征摘要】
1.一种耐800℃高温用纳米陶瓷涂料，其特征在于，所述纳米陶瓷涂料由以下重量份数的原材料组成：硅氧烷：32-40份聚乙烯醇缩丁醛液：12～22份无机颜料：10-18份填料：16-32份分散剂：0.5-1.4份流平剂：0.2-1份溶剂：3-6份。2.根据权利要求1所述的耐800℃高温用纳米陶瓷涂料，其特征在于，所述溶剂为无水乙醇、异丙醇、正丁醇中的至少一种。3.根据权利要求1所述的耐800℃高温用纳米陶瓷涂料，其特征在于，所述硅氧烷为甲基三甲氧基硅烷、甲基三乙氧基硅烷、二甲基二甲氧基硅烷中的至少一种。4.根据权利要求1所述的耐800℃高温用纳米陶瓷涂料，其特征在于，所述聚乙烯醇缩丁醛液选用异丙醇或正丁醇为溶剂，固含为10％。5.根据权利要求1所述的耐800℃高温用纳米陶瓷涂料，其特征在于，所述填料含有750℃熔点的高熔点玻璃粉。6.根据权利要求5所述的耐800℃高温用纳米陶瓷涂料，其特征在于，所述填料含有钛酸钾晶须、云母...