The invention discloses a composite fiber toughening foam insulation material, which is made up of the raw material of the following weight: polybenzo imidazole 5, phosphate Cellulose 3, 4, ethylene glycol mono 0.3 1, polyethylene wax 4 7, isobutyric acid sucrose 1 2, methyl benzene sulfonate 2 3, polystyrene 110 130 130, castor oil. Zinc 1, borax 2, 2 borax 4, coconut two ethanolamide 0.6 1, ammonium polyphosphate 3 5, and 7 foaming agent 7, this foaming material can play a good thermal insulation effect, good compatibility between the processed raw materials, and the added ammonium polyphosphate can improve the anti ignition and fire resistance of the finished product, and the zinc ricinoleate can improve the resistance. Thermal stability, polyethylene wax can improve the bond strength between raw materials, thereby improving the stability of finished products.
【技术实现步骤摘要】
一种复合纤维增韧发泡保温材料及其制备方法
本专利技术属于保温材料领域，具体涉及一种复合纤维增韧发泡保温材料及其制备方法。
技术介绍
聚苯乙烯泡沫材料是以聚苯乙烯树脂为基料，加入发泡剂等辅助材料，经加热发泡而成的轻质材料。它具有质轻、导热系数小、吸水率低、耐水、耐老化、耐低温、易加工、价廉质优等优点，但是聚苯乙烯泡沫保温材料在给人们的生活带来巨大方便的同时，其易燃性也给它的应用带来了一定的限制。聚苯乙烯泡沫本身是易燃材料，在火灾和高温条件下极易发生分解燃烧，并伴有大量毒气产生。因此，急需开展对聚苯乙烯泡沫保温材料火灾安全性方面的研究工作；发泡聚苯乙烯树脂的用途非常广泛，由于其具有高强度、质量轻、极佳的保温绝热性能和高吸收能量能力，可以用作各种仪表、贵重物品、精密仪器、蔬菜水果和水产品等的包装材料；而因为其具有热传导率低、吸水性小、电绝缘性好、隔音、防潮以及成型工艺简单等优良特性，而被广泛应用在道路桥梁的路基铺设和房屋建筑以及渔业捕捞和冷藏行业的保温材料等方面。其中，作为一种优良的建筑材料，发泡聚苯乙烯树脂主要用于建筑物的屋面和墙体，其作为外保温复合墙体具有十分良好的...
【技术保护点】
一种复合纤维增韧发泡保温材料，其特征在于，它是由下述重量份的原料组成的：聚苯并咪唑纤维5‑7、磷酸纤维素3‑4、乙二醇单丁醚0.3‑1、聚乙烯蜡4‑7、乙酸异丁酸蔗糖酯1‑2、对甲基苯磺酸2‑3、聚苯乙烯110‑130、蓖麻油酸锌1‑2、硼砂2‑4、椰油酸二乙醇酰胺0.6‑1、聚磷酸铵3‑5、发泡剂7‑12。
【技术特征摘要】
1.一种复合纤维增韧发泡保温材料，其特征在于，它是由下述重量份的原料组成的：聚苯并咪唑纤维5-7、磷酸纤维素3-4、乙二醇单丁醚0.3-1、聚乙烯蜡4-7、乙酸异丁酸蔗糖酯1-2、对甲基苯磺酸2-3、聚苯乙烯110-130、蓖麻油酸锌1-2、硼砂2-4、椰油酸二乙醇酰胺0.6-1、聚磷酸铵3-5、发泡剂7-12。2.根据权利要求1所述的一种复合纤维增韧发泡保温材料，其特征在于，所述的发泡剂为AC发泡剂。3.一种如权利要求1、2中任一所述的复合纤维增韧发泡保温材料的制备方法，其特征在于，包括以下步骤：(1)取聚苯并咪唑纤维，加入到其重量3-4倍的二甲基甲酰胺中，送入到130-140℃的恒温水浴中，保温搅拌10-20分钟，出料，加入乙二醇单丁醚，搅拌至常温，得纤维分散液；(2)取聚乙烯蜡，加入到其重量3-5倍的无水乙醇中，搅拌均匀，加入乙酸...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。