The invention belongs to the field of functional materials, and discloses a tear resisting buffer material and a preparation method and application thereof. According to the raw material weight, the buffer material includes 5 carbon nanotubes based polyether polyols, 100 polyether Voranol 3010, 3 portions of water, 1 silicone oil 2370, 0.3 copies of three ethylene two amine solution, 0.12 portion of stannous octanate and 41 TDI80/20. The mixture was then foamed at 60 C to produce a tear resistant buffer material. A series of carbon nanotube based polyether polyols are synthesized by the organic functionalization of the carbon nanotube surface, and the modified carbon nanotube can be filled into the system of the buffer material so as to prepare the buffer material with excellent tearing resistance.
【技术实现步骤摘要】
一种耐撕裂缓冲材料及其制备方法和应用
本专利技术属于功能材料领域，特别涉及一种耐撕裂缓冲材料及其制备方法和应用。
技术介绍
随着人们生活水平的不断提高以及对生活舒适度的不断追求，缓冲材料(也称慢回弹泡沫塑料或者黏弹性聚氨酯泡沫塑料)的使用范围逐年拓宽，用量也有较快的增长。缓冲材料最初由美国太空总署(NASA)于上世纪六十年代研发，主要是为了缓解宇航员所承受的压力，保护宇航员的脊椎，特别是航天飞机在返回和离开地面时宇航员所承受的压力。瑞典Fagerdala公司将其二次开发为民用(医用)产品，最先在医疗急救、监护系统中推广应用，继而在日本等注重健康的发达国家迅速普及。缓冲材料在我国的应用长期以来处于空白状态，近年来随着我国经济快速增长对高品质材料的需求，缓冲材料在家具、汽车配件、鞋材、运动器材、医疗器械等领域得到了广泛的应用。缓冲材料在其各个应用领域内的优异性能表现，均源于其材料特殊的黏弹特性，即材料在受到压力冲击时，既发生了满足胡克定律的弹性形变，也同时发生不可恢复的塑性变形，也就是说，缓冲材料的变形是这两种变形的有机组合。塑性变形会消耗掉大部分的冲击能，而弹性变形...
【技术保护点】
一种耐撕裂缓冲材料，其特征在于：该缓冲材料由以下按重量份数计的原料制备而成：
【技术特征摘要】
1.一种耐撕裂缓冲材料，其特征在于：该缓冲材料由以下按重量份数计的原料制备而成：2.根据权利要求1所述的一种耐撕裂缓冲材料，其特征在于：所述碳纳米管基聚醚多元醇的合成方法包括如下步骤：(1)酰氯化反应：称取15g羧基化碳纳米管，加入300mLSOCl2与5mLDMF中，在70℃条件下搅拌反应24h；冷却至室温后，将反应产物在N2保护下用无水THF洗涤过滤，直到溶液澄清；用N2吹干后将产物置于烘箱中，烘干并研磨得到黑色粉末状酰氯化碳纳米管；(2)碳纳米管基聚醚多元醇的制备：取10g步骤(1)所得酰氯化碳纳米管，加入300mL低聚聚醚多元胺溶液，110℃条件下搅拌反应7h；冷却至室温后，将...
【专利技术属性】
技术研发人员：郑春柏，魏巍，沃伊切赫斯坦尼斯瓦夫古托夫斯基，王小刚，王博伟，
申请(专利权)人：广东互典缓冲材料技术有限公司，
类型：发明
国别省市：广东,44