The present invention provides a free radical polymerization resin composition, which is characterized by containing free radical polymerized resin (A), air drying compound (B), free radical polymerized monomer (C) and asphalt (D), and the content of the above asphalt (D) is 0.01 of the total of 100 of the above resin (A), the above compounds (B) and the above monomer (C). To 25 mass fraction, the bottom coating and backing plate waterproof structure obtained from the polymerized resin composition of the free radical are also provided. The free radical polymerized resin composition of the invention is a material with excellent adhesion between the waterproof layer and the asphalt pavement layer. In addition, the room temperature drying is also excellent, and can also be sprayed, so it can also improve the operability of end construction.
【技术实现步骤摘要】
自由基聚合性树脂组合物、底涂料及垫板防水结构体
本专利技术涉及常温干燥性、以及防水层与沥青铺装层的层间粘接性优异的自由基聚合性树脂组合物、以及使用该自由基聚合性树脂组合物而得到的底涂料及垫板防水结构体。
技术介绍
近来，随着日益增加的交通负荷、防冻剂的撒布，以高速公路为首的公路桥梁垫板的提前劣化变得明显起来。作为该提前劣化的机理，可以认为是由于在沥青铺装和钢筋混凝土垫板中产生的裂纹，使得雨水、防冻剂等侵入到结构物中而腐蚀钢筋，因而降低结构物的耐久性。作为提高公路桥梁垫板的耐久性的手法，对依次层叠垫板层、防水层、沥青铺装层而构成的垫板防水结构体进行过各种研究。另外，由于上述防水层和沥青层缺乏粘接性，因此还研究过各种用于提高层间粘接性的方法。作为上述方法，例如研究过向上述防水层与沥青铺装层的层间插入多孔性的热塑性树脂片的方法(例如参照专利文献1。)、使用聚氨酯系反应性热熔胶粘剂的方法(例如参照专利文献2。)。但是，均不能说具有足够的防水层与沥青铺装层的层间粘接性，另外还可以指出如下的缺点，即，在插入多孔性的热塑性树脂片的方法中，由于使用片材，因此端部施工困难，在使用聚...
【技术保护点】
一种自由基聚合性树脂组合物，其特征在于，含有自由基聚合性树脂(A)、空气干燥性化合物(B)、自由基聚合性单体(C)及沥青(D)，所述空气干燥性化合物(B)是使选自包含环状不饱和脂肪族多元酸及其衍生物的化合物、包含具有α位氢的烯丙基醚基的化合物、利用多元醇与干性油的酯交换反应而得到的醇解化合物、及包含具有羟基的二环戊二烯基的化合物中的1种以上的具有空气干燥性赋予基团的化合物(b1)与选自α，β‑不饱和二元酸、多元醇、芳香族饱和二元酸及其酸酐中的1种以上的化合物(b‑2)进行加成反应或酯化反应而得的化合物，所述沥青(D)的含量相对于所述自由基聚合性树脂(A)、所述空气干燥性化合...
【技术特征摘要】
2012.12.14 JP 2012-2734411.一种自由基聚合性树脂组合物，其特征在于，含有自由基聚合性树脂(A)、空气干燥性化合物(B)、自由基聚合性单体(C)及沥青(D)，所述空气干燥性化合物(B)是使选自包含环状不饱和脂肪族多元酸及其衍生物的化合物、包含具有α位氢的烯丙基醚基的化合物、利用多元醇与干性油的酯交换反应而得到的醇解化合物、及包含具有羟基的二环戊二烯基的化合物中的1种以上的具有空气干燥性赋予基团的化合物(b1)与选自α，β-不饱和二元酸、多元醇、芳香族饱...