The invention discloses a preparation method of a sustained-release scale inhibitor, and the preparation steps include: 1) preparing a saturated aqueous solution of cyclodextrin, 2) adding a scale inhibitor to the cyclodextrin saturated aqueous solution of the cyclodextrin at the stirring speed of 25, 50 and 150 250r/min, and continuously stirring for 24 hours after 24 hours of stirring, and centrifugation to separate the sediment. The residual scale inhibitor was washed with a concentration of 95% ethanol and dried naturally at room temperature. The preparation method of the invention is simple, and the cyclodextrin is used as a sustained-release carrier and a scale inhibitor to form the inclusion compound, so as to achieve the goal of slow release of the scale inhibition active component, and play the role of controlling the slow release and scale inhibition.
【技术实现步骤摘要】
一种缓释阻垢剂的制备方法及缓释阻垢剂
本专利技术涉及一种缓释阻垢剂的制备方法以及由此制得的缓释阻垢剂，属于阻垢缓释及水处理
技术介绍
硬水指的是含有较多可溶性钙镁化合物的水，其一直影响着我们的日常生活品质并在各方面给人们的生活造成诸多不便。硬水烧开后会出现白沫浮在水的表面上或沉淀在水壶底部，饮用后会造成胃肠功能紊乱；而用硬水清洗衣物的话，水力的钙镁离子会和肥皂结合生成脂肪酸钙和脂肪酸镁的絮状沉淀，降低去污能力，不仅浪费肥皂还损伤衣物；而使用硬水沐浴，则会造成皮肤不滑爽、头发晦暗等问题。此外，用水硬度过高，容易导致涉水家用电器管路或内壁表面结构，而由于水垢的导热性很差，进而往往会导致受热面传热能力恶化，从而造成燃料或电力的浪费，且缩短电器的使用寿命；如果水垢胶结于热水器或锅炉内壁，由于热胀冷缩和受热不均匀，极大地增加了热水器或锅炉爆裂甚至爆炸的危险性。当前，针对硬水的处理，大多采用离子交换技术、膜分离技术、分子筛吸附技术等。其中，离子交换技术是一种成熟的传统工艺，但树脂易受污染氧化而导致失效，再生频繁，并且会置换出钠离子，导致经该技术处理后的水不适宜长期饮...
【技术保护点】
一种缓释阻垢剂的制备方法，其特征在于：包括以下制备步骤：1)配制环糊精的饱和水溶液；2)在25‑50℃、150‑250r/min的搅拌速度下向步骤1)的环糊精饱和水溶液中加入阻垢剂，持续搅拌12‑24小时后静置24小时，离心分离出沉淀物并以浓度为95％的乙醇洗涤去除残余的阻垢剂后于室温下自然晾干，即得所述缓释阻垢剂。
【技术特征摘要】
1.一种缓释阻垢剂的制备方法，其特征在于：包括以下制备步骤：1)配制环糊精的饱和水溶液；2)在25-50℃、150-250r/min的搅拌速度下向步骤1)的环糊精饱和水溶液中加入阻垢剂，持续搅拌12-24小时后静置24小时，离心分离出沉淀物并以浓度为95％的乙醇洗涤去除残余的阻垢剂后于室温下自然晾干，即得所述缓释阻垢剂。2.根据权利要求1...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。