The invention provides a dyeing and finishing process of tissue foam fabric. The fabric is made by 40S and 40/2S, and the following steps are made by the following steps: the burning, the retreating of the long car, the oxygen bleaching, the mercerization, the whitening, the drawing of the drawing, the digital printing, the steaming, the water washing, the softness of the air flow and the super soft treatment, in which the scraper pressure of the long car is retreated. To zero, the pressure of the desizing saturated steam tank is 0.15 ~ 0.25Mpa, the desizing enzyme concentration is 0.17 ~ 0.25g/l, the NaOH concentration is 20g/l, and the speed is 70m/min. In the mercerizing process, the alkali concentration is 140g/l to 150g/l, the cloth width is the upper limit of the finished product width; the drawing process is over feed to the fabric from 5% to 8%, and the processing temperature in the flow softening process is used. At 115 C, the dosage of softener is 3 ~ 8g/l and the treatment time is 20 ~ 35min, the speed of the super soft treatment process is 10 ~ 25m/min, the temperature is 100~120, and the other procedures are used routinely. The invention can keep the bubbles on the fabric to the maximum, and assist with mercerizing, drawing, soft and super soft treatment, so as to ensure the foaming effect of the fabric and the soft and plump feeling of the fabric.
【技术实现步骤摘要】
一种组织起泡面料的染整加工工艺
本专利技术涉及一种组织起泡面料的染整加工工艺，属于纺织染整
技术介绍
目前所生产的起泡面料在染整加工后所得的面料起泡不均匀，起泡效果差，甚至出现无泡现象；进过多次搓洗后，泡泡会逐渐平坦；且面料手感偏硬，不能满足客户及市场的需求。
技术实现思路
本专利技术目的在于提供一种能解决上述问题、保证起泡效果和手感柔软丰满的组织起泡面料的染整加工工艺。其技术方案为：一种组织起泡面料染整加工工艺，坯布采用40S与40/2S织造而成，其特征在于采用以下步骤：烧毛→长车退煮→氧漂→丝光→增白洗→拉幅上浆→数码印花→蒸化→水洗→气流柔软→超柔软处理，其中长车退煮工序中，刮刀压力为零，退浆饱和蒸汽罐压力为0.15～0.25Mpa，退浆酶浓度为0.17～0.25g/l，NaOH浓度20g/l，车速70m/min；丝光工序中，碱浓度为140g/l～150g/l，落布幅宽为成品幅宽上限；拉幅上浆工序对面料进行5％～8％的超喂；气流柔软工序中加工温度为115℃，柔软剂用量3～8g/l，处理时间20～35min；超柔软处理工序中车速10～25m/min，温度...
【技术保护点】
一种组织起泡面料染整加工工艺，坯布采用40S与40/2S织造而成，其特征在于采用以下步骤：烧毛→长车退煮→氧漂→丝光→增白洗→拉幅上浆→数码印花→蒸化→水洗→气流柔软→超柔软处理，其中长车退煮工序中，刮刀压力为零，退浆饱和蒸汽罐压力为0.15～0.25Mpa，退浆酶浓度为0.17～0.25g/l，NaOH浓度20g/l，车速70m/min；丝光工序中，碱浓度为140g/l～150g/l，落布幅宽为成品幅宽上限；拉幅上浆工序对面料进行5％～8％的超喂；气流柔软工序中加工温度为115℃，柔软剂用量3～8g/l，处理时间20～35min；超柔软处理工序中车速10～25m/min，...
【技术特征摘要】
1.一种组织起泡面料染整加工工艺，坯布采用40S与40/2S织造而成，其特征在于采用以下步骤：烧毛→长车退煮→氧漂→丝光→增白洗→拉幅上浆→数码印花→蒸化→水洗→气流柔软→超柔软处理，其中长车退煮工序中，刮刀压力为零，退浆饱和蒸汽罐压力为0.15～0.25Mpa，退浆酶浓度为0.17～0.25g/l，NaOH浓度20g/l，车速70m/min；丝光工序中，碱浓度为140g/l～150g/l，落布幅宽为成品幅宽上限；拉幅上浆工序对面料进行5％～8％的超喂；气流柔软工序中加工温...
【专利技术属性】
技术研发人员：张战旗，齐元章，李智，牛纪玲，宋琳，仲伟浩，刘桂杰，
申请(专利权)人：鲁丰织染有限公司，
类型：发明
国别省市：山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。