一种钢铁除油除锈除氧化皮清洗剂制造技术

本发明专利技术公开了一种高效环保的钢铁除油除锈除氧化皮清洗剂，其组成包括磷酸30‑45％；有机膦酸7‑11％；乳化剂2‑3％；促进剂0.2‑0.5％；抑制剂5‑8％；以及余量的水。本发明专利技术提供的钢铁除油除锈除氧化皮清洗剂，配合超声波清洗设备，可以快速去除钢铁表面油污、浮锈；通过延长超声时间，可以去除钢铁表面顽固锈迹以及退火等产生的氧化皮；除锈、除氧化皮后钢材不会产生氢脆，可以取代传统的盐酸型清洗剂。

A steel cleaning agent for removing rust and removing rust

The invention discloses an efficient and environmentally friendly cleaning agent for removing rust and removing rust in steel, which consists of 30 phosphoric acid 45%, 7 organic phosphonic acid, 11%, 2 emulsifier 3%, accelerator 0.2, 0.5%, inhibitor 5 8%, and waste water. This invention can remove oil pollution and floating rust on steel surface quickly, with ultrasonic cleaning equipment and ultrasonic cleaning equipment. By prolonging ultrasonic time, it can remove the oxide skin from steel surface stubborn rust and annealing, and the steel will not produce hydrogen embrittlement after removing rust and oxide skin. Generation of traditional hydrochloric acid cleaning agent.

【技术实现步骤摘要】
一种钢铁除油除锈除氧化皮清洗剂
本专利技术涉及金属表面处理
，具体涉及一种用于钢铁表面的除油、除锈、除氧化皮清洗剂。
技术介绍
现阶段我国工业发展速度迅猛，各领域中钢铁使用量逐年增加，钢铁除锈过程中造成的空气与环境污染日益严重。现有钢铁除锈方法有喷砂、机械打磨、除锈剂等，但都存在这样那样的问题和缺陷。喷砂：使用喷砂机，成本高，投资大，耗电能，有噪音，喷出的粉末污染空气。机械打磨：使用机电设备，除锈效果差，有死角(设备存在处理不到的边角)，有噪音，有污染。强酸除锈：有酸气雾，易产生雾霾，污染空气和环境，对人体皮肤及呼吸系统都有极大危害；处理时间过长，会对钢铁工件整体有腐蚀，改变工件尺寸，易返锈。传统除锈工艺一般使用工业盐酸、工业硫酸等无机酸除锈，虽然成本低廉，但环境污染大、废水处理成本高，而且受公安易制毒化学品管制的制约，使得用户在除锈工艺的报批、环保达标成为一大难题。现有钢铁环保除锈剂通常还是会使用有机膦络合或者氢氟酸等进行除锈，该类除锈剂对返锈产品可以达到一定的除锈效果，但是对顽固锈迹以及退火等产生的氧化皮的除锈基本没有效果。
技术实现思路
针对现有技术中存在的问题，本专利技术旨本文档来自技高网...

【技术保护点】
一种钢铁除油除锈除氧化皮清洗剂，其特征在于，所述钢铁除油除锈除氧化皮清洗剂的各组分及其含量如下：

【技术特征摘要】
1.一种钢铁除油除锈除氧化皮清洗剂，其特征在于，所述钢铁除油除锈除氧化皮清洗剂的各组分及其含量如下：2.根据权利要求1所述的一种钢铁除油除锈除氧化皮清洗剂，其特征在于，所述的有机膦酸为二乙烯三胺五甲叉膦酸、乙二胺四甲叉膦酸、氨基三甲叉膦酸、羟基乙叉二膦酸中的一种或多种。3.根据权利要求1所述的一种钢铁除油除锈除氧化皮清洗剂，其特征在于，所述的乳化剂为烷基酚聚氧乙烯醚、异构醇聚氧乙烯醚中的一种或多种。4.根据权利要求3所述的一种钢铁除油除锈除氧化皮清洗剂，其特征在于，所述烷基酚聚氧乙烯醚选自TX-...

【专利技术属性】
技术研发人员：陈珍珍，胡磊，王艳，
申请(专利权)人：苏州禾川化学技术服务有限公司，
类型：发明
国别省市：江苏,32