An alkali free accelerator is related to concrete admixture, especially to an alkali free accelerator. In this invention, aluminum sulfate is used as base material to prepare alkali free accelerator, and in the system, the acid and alkali environment of acid solvent dispensing system such as methacrylic acid and phosphoric acid is added to the system. In addition, the auxiliary materials such as sodium fluoride, calcium formate, triethanolamine and hydroxyethyl carboxymethyl cellulose are added to enhance the later strength of concrete. On the basis of corroding concrete steel materials, the later strength of the project can be guaranteed not to be lost. In the system, xylene is added as a activator to accelerate the reaction process. The invention can ensure that the solidification rate of concrete is accelerated without the introduction of alkali and does not affect the later strength of concrete.
【技术实现步骤摘要】
一种无碱速凝剂
本专利技术涉及到混凝土外加剂，特别涉及一种无碱的速凝剂。
技术介绍
速凝剂的运用能够有效的减少水泥的凝结时间从而减少工期，加快工程进度。而自20世纪30年代首次专利技术速凝剂以来，速凝剂的发展以及运用飞快。但是我国速凝剂的发展却比较缓慢，我国的速凝剂主要以“红星-Ι型”和“728型”为代表，但是就目前我国市面上的速凝剂来看，主要以有碱速凝剂为主。中国专利技术专利号CN1407954A公布了一种速凝剂的制备，其通过将硫酸铝溶于水中以生成氢氧化铝再加入含胺的水中，又以羧酸、磷酸及盐作为稳定剂制备速凝剂。此速凝剂虽然速凝时间短，能使混凝土有良好的强度，并且能够抵抗温度的变化，但是在实际的生产制备过程中生成了中间生成了氢氧化铝，在体系中碱性物质的生成会造成体系的PH值难以控制，从而无法确保产品的最终效果。中国建筑材料科学研究总院专利CN201110112424公开了一种以硫酸铝为基料，有机胺类为粘度调节剂制备的无碱液体速凝剂，此速凝剂能够有效的减少混凝土凝结的时间并且还能够提高喷射层厚度，但是通过实际的检测发现使用此速凝剂的混凝土在使用的后期会造成强度损失...
【技术保护点】
一种无碱速凝剂，主要由硫酸铝、水、硅酸钠、三乙醇胺、二甲苯、羟乙基羧甲基纤维素、氟化钠、甲酸钙组成，其特征在于，组分按重量份计硫酸铝50‑60份、水15‑25份、氟化钠7‑13份、二甲苯0.4‑0.6份、硅酸钠4‑6份、三乙醇胺0.4‑0.6份、甲酸钙0.2‑0.4份、羟乙基羟甲基纤维素0.2‑0.4份。
【技术特征摘要】
1.一种无碱速凝剂，主要由硫酸铝、水、硅酸钠、三乙醇胺、二甲苯、羟乙基羧甲基纤维素、氟化钠、甲酸钙组成，其特征在于，组分按重量份计硫酸铝50-60份、水15-25份、氟化钠7-13份、二甲苯0.4-0.6份、硅酸钠4-6份、三乙醇胺0.4-0.6份、甲...
【专利技术属性】
技术研发人员：阿光强，郭军，阿光城，徐兴爱，李金梅，
申请(专利权)人：云南森博混凝土外加剂有限公司，
类型：发明
国别省市：云南,53