一种三元复合微波萃取剂及其应用制造技术

本发明专利技术涉及高分子领域的一种三元复合微波萃取剂及其应用。所述的三元复合微波萃取剂，由二甲苯、二氯甲烷和正己烷组成，所述二甲苯、二氯甲烷和正己烷的体积比为100:(40‑60):(10‑20)。所述三元复合微波萃取剂的针对性强，专用于萃取PVC中的增塑剂PAEs，且萃取率高；同时本发明专利技术所述的三元复合微波萃取剂的沸点相对较低，其对温度和压力的要求较低，不需要很高的微波萃取温度和压力即可实现最大萃取，降低了爆罐等风险。

A three element composite microwave extractant and its application

The invention relates to a three component composite microwave extractant in the polymer field and its application. The three - element composite microwave extractant consists of xylene, dichloromethane and n-hexane. The volume ratio of xylene, dichloromethane and hexane is 100: (40, 60): (10, 20). The three element composite microwave extractant is highly targeted and is specially designed to extract the plasticizer PAEs in PVC, and the extraction rate is high; at the same time, the boiling point of the three element compound microwave extractant is relatively low, the requirement for temperature and pressure is low, and the maximum extraction can be achieved without high microwave extraction temperature and pressure. Lower the risk of detonating the tank.

【技术实现步骤摘要】
一种三元复合微波萃取剂及其应用
本专利技术属于高分子领域，具体涉及一种三元复合微波萃取剂及其应用。
技术介绍
聚氯乙烯(Polyvinylchloride，简称PVC)由氯乙烯在引发剂作用下聚合而成的热塑性树脂，是五大通用塑料之一。增塑剂添加至高分子材料中能改善材料的塑性，增强高分子材料的柔软性，在日常用品中应用极其广泛，如包装袋、桌垫、壁纸、玩具等。当身体或者生产生活中的某些液体与含有增塑剂的高分子材料接触时，微量增塑剂会从高分子材料中提取出来，若增塑剂含量过高，长期接触则会对身体造成一定伤害。邻苯二甲酸酯(PAEs)，又称酞酸酯，是邻苯二甲酸形成酯的统称。在塑料工业中具有广泛的应用，经常被添加到塑料中作为增塑剂。当被用作塑料增塑剂时，一般指的是邻苯二甲酸与含有4-15个碳的醇形成的酯。由于PAEs与聚合物本体仅通过氢键或范德华力结合，因此会在使用过程中不断释放出来而转移到周围环境中，成为广泛存在于大气、水体、土壤中的有机污染物，从而普遍存在于人类生活的环境中。PAEs是典型的环境雌激素污染物，通过植物吸收进入植物体内，会发生生物富集，长期接触会影响人体内分泌，导致畸形、癌变和致突本文档来自技高网...

【技术保护点】
一种三元复合微波萃取剂，其由二甲苯、二氯甲烷和正己烷组成。

【技术特征摘要】
1.一种三元复合微波萃取剂，其由二甲苯、二氯甲烷和正己烷组成。2.根据权利要求1所述的萃取剂，其特征在于，所述二甲苯、二氯甲烷和正己烷的体积比为100:(40-60):(10-20)。3.根据权利要求2所述的萃取剂，其特征在于，所述二甲苯、二氯甲烷和正己烷的体积比为100:(50-60):(10-20)。4.一种采用权利要求1-3任一项所述的萃取剂萃取聚氯乙烯材料中邻苯二甲酸酯的方法。5.根据权利要求4...

【专利技术属性】
技术研发人员：胡法，孙晋，华晔，武志军，熊志敏，魏若奇，
申请(专利权)人：中国石油化工股份有限公司，中国石油化工股份有限公司北京化工研究院，
类型：发明
国别省市：北京,11