The invention discloses a kind of bismuth free stainless steel flux cored wire. According to the weight percentage, the flux of the bismuth free stainless steel flux cored wire has the following components: Bi < 0.001%, titanium oxide 5 ~ 15%, silicon oxide 1 ~ 3%, zirconia 1 to 3%, manganese oxide 0.1 ~ 1%, iron oxide 0.1 ~ 1%, manganese 1 ~ 2%, silicon metal 0.1 ~ 1%, nickel metal 8 ~ 14%, chromium metal 18 ~ 25%, fluoride 0.1 ~ 1.5%, rare earth element 0.01 ~ 0.5%, the allowance is Fe. The bismuth free austenitic stainless steel flux cored wire has Bi less than 5ppm, which can effectively reduce the risk of thermal cracking of austenitic stainless steel joint, and improve the safety production of pressure vessel and petrochemical industry.
【技术实现步骤摘要】
一种无铋不锈钢药芯焊丝
本专利技术属于焊接材料领域，特别涉及一种无铋奥氏体不锈钢药芯焊丝。
技术介绍
不锈钢药芯焊丝具有优异的焊接性，稳定的物化性能，耐蚀性优异，合金成分调整周期短等特点，目前行业应用越来越广泛，种类也越来越趋于齐全，也深入一些特殊行业领域的应用，如压力容器及核电等。普通的不锈钢药芯焊丝为了获得良好的脱渣性，会通过添加过量的Bi元素来获得，Bi含量添加不足，则脱渣性就会极差，但在不锈钢药芯焊丝焊接奥氏体不锈钢的生产过程中，焊接接头在高于700℃的环境中工作一段时间后会产生热裂纹，经过研究发现Bi元素为影响的主要原因，故为改善奥氏体不锈钢的热裂纹倾向，把不锈钢药芯焊丝熔敷金属中的Bi含量控制在极低的范围内，但是这样一来又容易因Bi含量过低而造成脱渣不好。
技术实现思路
为了解决以上问题，本专利技术公开一种无铋奥氏体不锈钢药芯焊丝，其熔敷金属中Bi≤5ppm，另以稀土元素替代部分Bi，既有效地降低奥氏体不锈钢接头产生热裂的风险，又保证良好的脱渣性。为实现上述技术目的，本专利技术的技术方案是：一种无铋不锈钢药芯焊丝，由焊药和钢带构成，按照重量百分比，所述无铋...
【技术保护点】
一种无铋不锈钢药芯焊丝，由钢带及焊药组成，其特征在于，按照重量百分比，所述无铋不锈钢药芯焊丝的焊药具有以下组成：Bi≤0.001％，氧化钛5～15％，氧化硅1～3％，氧化锆1～3％，氧化锰0.1～1％，氧化铁0.1～1％，锰金属1.0～2.0％，硅金属0.1～1.0％，镍金属8.0～14.0％，铬金属18.0～25.0％，氟化物0.1～1.5％，稀土元素0.01～0.5％，余量为Fe。
【技术特征摘要】
1.一种无铋不锈钢药芯焊丝，由钢带及焊药组成，其特征在于，按照重量百分比，所述无铋不锈钢药芯焊丝的焊药具有以下组成：Bi≤0.001％，氧化钛5～15％，氧化硅1～3％，氧化锆1～3％，氧化锰0.1～1％，氧化铁0.1～1％，锰金属1.0～2.0％，硅金属0.1～1.0％，镍金属8.0～14.0％，铬金属18.0～25.0％，氟化物0.1～1.5％，稀土元素0.01～0.5％，余量为Fe。2.如权利要求1所述的无铋不锈钢药芯焊丝，其特征在于，所述氟化物为氟化钠、氟化锂、冰晶石、铁氟龙、氟化硅、氟化锆中的一种或几种。3.如权利要求1所述的无铋不锈钢药芯焊丝，其特征在于，所述无铋不锈钢药芯焊丝的熔敷金属中Bi≤5ppm。...
【专利技术属性】
技术研发人员：蔡鸿祥，庄石城，叶桂林，周峙宏，
申请(专利权)人：昆山京群焊材科技有限公司，
类型：发明
国别省市：江苏,32