The present invention relates to the field of catalyst, and discloses a load type carrier and its preparation method and application. The carrier comprises a ceramic fiber and an alumina coating coated on the surface of the ceramic fiber. The invention also provides a preparation method of the carrier, and a load carrier prepared by the method and its application. The carrier preparation process provided by the invention is simple, and the carrier provided by the invention is used in the preparation of catalyst with catalytic organic waste gas combustion function, and has high catalytic activity.
【技术实现步骤摘要】
一种负载型载体及其制备方法和应用
本专利技术涉及催化剂领域，具体地，涉及一种负载型载体及其制备方法，以及由该方法制备得到的负载型载体及其应用。
技术介绍
陶瓷纤维是一种纤维状轻质材料，具有重量轻、耐高温、热稳定好、导热率低、比热小及耐机械震动、强度高、抗热冲击性好、耐化学腐蚀等特点，在机械、冶金、化工、石油、陶瓷、玻璃、电子等行业都得到了广泛的应用，同时，它也是是一种理想的高温过滤材料。近年来已经使用陶瓷纤维成功开发出各种过滤器，例如，烛式过滤器、织物过滤器和复合过滤器，被广泛应用于火力发电厂金属冶炼厂化工厂的消烟除尘，同时，在有机废气净化领域也具有广阔的应用前景。CN103806990A公开了一种陶瓷纤维催化剂载体的汽车尾气处理器制备方法，该方法将铈、锆、镧、锶和钴的无机盐溶液加入溶胶形成剂经搅拌均匀后，再加入胶粒悬浮剂，得到稳定的催化剂溶胶。将陶瓷纤维棉柱，浸入催化剂溶胶中，得到表面粘附催化剂胶体的陶瓷纤维棉柱；再经干燥和煅烧得到负载催化剂的陶瓷纤维棉柱，装入带有内保温层的金属壳中，即得到汽车尾气净化器。该方法制备的陶瓷纤维催化剂强度低，不耐机械振动，且活性组...
【技术保护点】
一种负载型载体，其特征在于，该载体包括陶瓷纤维和涂覆在所述陶瓷纤维表面的氧化铝涂层。
【技术特征摘要】
1.一种负载型载体，其特征在于，该载体包括陶瓷纤维和涂覆在所述陶瓷纤维表面的氧化铝涂层。2.根据权利要求1所述的载体，其中，以载体的总重量为基准，所述陶瓷纤维的含量为75.5-90.5重量％，优选为82.5-90.5重量％；所述氧化铝涂层的含量为9.5-24.5重量％，优选为9.5-17.5重量％。3.根据权利要求1或2所述的载体，其中，所述陶瓷纤维的直径为2-5μm；和/或，所述氧化铝涂层的厚度为0.2-0.8μm。4.一种制备负载型载体的方法，其特征在于，该方法包括：在超声条件下，将陶瓷纤维浸渍于氧化铝浆料中，然后依次进行干燥和焙烧。5.根据权利要求4所述的方法，其中，所述氧化铝浆料的固含量为5-45重量％，优选为15-25重量％；pH值为4-6.5，优选为4-6。6.根据权利要求4或5所述的方法，其中，所述氧化铝浆料的制备方法包括：在酸性条件下，将铝源与水的混合物进行球磨，得到氧化铝浆料；优选地，所述铝源与水的用量的重量比为1：4-20。7.根据权利要求6所述的方法，其中，所述铝源选自拟薄水铝石、三水铝石、氢氧化铝和铝溶胶中的至少一种。8.根据权利要求6所述的方法，其中，所述球磨的条件包括：转速为300-600r/min，球磨时间为24-36h；优...
【专利技术属性】
技术研发人员：王育，彭晖，乐毅，刘小波，杨沙沙，刘海江，马天石，
申请(专利权)人：中国石油化工股份有限公司，中国石油化工股份有限公司北京化工研究院，
类型：发明
国别省市：北京,11