防锈添加剂及其对连续退火后的冷轧卷的防锈用途制造技术

本发明专利技术公开了一种防锈添加剂及其对连续退火后的冷轧卷的防锈用途，以质量百分比计，该防锈添加剂由如下组分组成：植酸：30～50％，单宁酸：30～50％，十八胺：10～20％，钼酸钠：3～6％，钨酸钠：3～6％。将连续退火后的冷轧卷浸渍于加入有该防锈添加剂的漂洗液中处理，与未经该漂洗液漂洗的冷轧卷相比，漂洗处理后的冷轧卷延迟了开始锈蚀的时间并减小了锈蚀程度。

Antirust additive and its anticorrosive use for cold rolled rolls after continuous annealing

The invention discloses an anti rust additive and anti rust on cold roll uses after continuous annealing process, by weight percentage of the anti rust additive which comprises the following components: phytic acid: 30 ~ 50%, 30 ~ 50%, eighteen: tannic acid amine: 10 ~ 20%, 3 ~ 6%, sodium molybdate: sodium tungstate: 3 ~ 6%. The cold rolled strip after continuous annealing is impregnated in the rinsing liquid added with the rust inhibitor. Compared with the cold rolled strip without rinsing the rinsing liquid, the cold rolling coil after rinsing treatment delays the time of starting rust and reduces the degree of rust.

【技术实现步骤摘要】
防锈添加剂及其对连续退火后的冷轧卷的防锈用途
本专利技术涉及一种防锈添加剂，属于有机化合物
，具体地涉及一种防锈添加剂及其对连续退火后的冷轧卷的防锈用途。
技术介绍
连续退火机组为把冷轧后的电解清洗、连续炉退火、钢卷冷却、调质轧制(平整)和精整检查等单独的生产工序联结成一条生产机组，实现连续化生产，简称CAPL，其具有如下优点：(1)产品质量好，板形平直，表面清洁，性能均匀；(2)成材率高，不会产生罩式退火易出项的粘结、折边等缺陷，成材率可提高2～3％；(3)品种多样化，除了能生产罩式退火的全部品种外，还可以生产高强度板、电工板等；(4)布置紧凑、占地面积小；(5)生产周期短，交货迅速，节能20％以上，节省劳动力，生产成本低。基于连续退火机组的上述优点，其在钢板生产中得到了较为广泛的应用。众所周知，退火环节决定钢板的表面构造和本体组织，而钢板锈蚀行为对本体组织并不敏感，主要对钢板的表面构造敏感，因此，退火环节对锈蚀的影响主要体现在钢板的表面构造上。这是因为连续退火工艺使得Si、Mn等易氧化元素富集于钢板表面，导致表面氧化膜不完整，表面活性较大。与此同时，连续退火后的钢卷较易受到本文档来自技高网...

【技术保护点】
一种防锈添加剂，其特征在于：以质量百分比计，它由如下组分组成：植酸：30～50％，单宁酸：30～50％，十八胺：10～20％，钼酸钠：3～6％，钨酸钠：3～6％。

【技术特征摘要】
1.一种防锈添加剂，其特征在于：以质量百分比计，它由如下组分组成：植酸：30～50％，单宁酸：30～50％，十八胺：10～20％，钼酸钠：3～6％，钨酸钠：3～6％。2.根据权利要求1所述的防锈添加剂，其特征在于：它由如下组分组成：植酸：36％，单宁酸：43％，十八胺：13％，钼酸钠：4％，钨酸钠：4％。3.一种权利要求1所述的防锈添加剂对连续退火后的冷轧卷的防锈用途。4.根据权利要求3所述的防锈添加剂对连续退火后的冷轧卷的防锈用途，其特征在于：将防锈添加剂加入到漂洗水中，混合均匀后得到漂洗液，控制所述漂洗液中防锈添加剂的质量百分比含量为0....

【专利技术属性】
技术研发人员：黄先球，郎丰军，庞涛，彭浩，程鹏，马颖，宋建红，黄菲，何锐，李安平，
申请(专利权)人：武汉钢铁有限公司，
类型：发明
国别省市：湖北,42