A preparation method of a laminated board, which belongs to the field of material preparation. Includes the following steps: sand grinding dispersion machine will acicular wollastonite powder dispersed in the phenolic resin and tung oil modified phenolic resin blend glue, coated on the surface of fine cotton; cotton will be placed in an oven baked; the amount of adhesive resin solution and time adjustment; cutting tape after baking, preheating in flat vulcanizing machine, and heating and pressurizing. Effective by improving the preparation process of laminated board, simplified, easy to operate more preparation process of making, the laminated board can have good thermal stability, impact strength in both transverse and longitudinal two directions is greatly improved, the preparation method saves the process cost of laminated board of the invention wherein, suitable for use.
【技术实现步骤摘要】
一种酚醛层压布板的制备方法
本专利技术属于材料制备领域，尤其涉及一种酚醛层压布板的制备方法。
技术介绍
随着科技的快速发展，新的材料与技术被用到了生活的各个方面，伴随人们出于对于新产品的功能、环保等方面的新要求，各种新的制备工艺也不断出现。酚醛树脂作为三大通用树脂之一，具有良好的粘结性，固化后的酚醛树脂具有较高的耐热性能、良好的介电性能、优异的耐烧蚀性能和较好的力学性能，但是固化后酚醛树脂的最大缺点是脆性大，耐冲击性不好。
技术实现思路
本专利技术旨在解决上述问题，提供一种酚醛层压布板的制备方法。一种酚醛层压布板的制备方法，其特征在于包括如下步骤：（1）用砂磨分散机将针状硅灰石粉均匀分散在不同配比的甲阶酚醛树脂和桐油改性酚醛树脂共混胶液中，将树脂胶液涂刷于细棉布表面，使其均匀浸渍；（2）将浸渍后的棉布置于烘箱中烘焙；调整树脂胶液的上胶量，使烘焙后上胶布树脂的质量分数控制在45%～50%；（3）调整烘培时间，使烘焙后上胶布可溶性树脂质量分数控制在93%～98%，挥发物质量分数控制在2%～4%；（4）裁剪烘焙后的上胶布，叠成24层，先在平板硫化机上预热，再根据流胶情况加温...
【技术保护点】
一种酚醛层压布板的制备方法，其特征在于包括如下步骤：（1）用砂磨分散机将针状硅灰石粉均匀分散在不同配比的甲阶酚醛树脂和桐油改性酚醛树脂共混胶液中，将树脂胶液涂刷于细棉布表面，使其均匀浸渍；（2）将浸渍后的棉布置于烘箱中烘焙；调整树脂胶液的上胶量，使烘焙后上胶布树脂的质量分数控制在45%～50%；（3）调整烘培时间，使烘焙后上胶布可溶性树脂质量分数控制在93%～98%，挥发物质量分数控制在2%～4%；（4）裁剪烘焙后的上胶布，叠成24层，先在平板硫化机上预热，再根据流胶情况加温加压。
【技术特征摘要】
1.一种酚醛层压布板的制备方法，其特征在于包括如下步骤：（1）用砂磨分散机将针状硅灰石粉均匀分散在不同配比的甲阶酚醛树脂和桐油改性酚醛树脂共混胶液中，将树脂胶液涂刷于细棉布表面，使其均匀浸渍；（2）将浸渍后的棉布置于烘箱中烘焙；调整树脂胶液的上胶量，使烘焙后上胶布树脂的质量分数控制在45%～50%；（3）调整烘培时间，使烘焙后上胶布可溶性树脂质量分数控制在93%～98%，挥发物质量分数控制在2%～4%；（4）裁剪烘焙后的上胶布，叠成24层，先在平板硫化...