The method of processing forming an artificial stone texture; comprises the following steps: A, cloth, raw material mixture in the mold is applied to sheet metal products, has the shape of the slab; B, applied to the extrusion pressure plate presses; C, giving applying at least one layer of cloth pigment, the pigment on the surface of sheet metal according to the design, or path of the final product texture, giving at least a uniform layer of pigment in the corresponding position of the surfaces of the plates; D, interlayer mixing, according to the set route of final product texture, mixing in surface of all or partial position corresponding to the corresponding position, and the mixing between pigment and raw material mixture. The product presents a more natural and truthful texture.
【技术实现步骤摘要】
一种人造石板纹理的加工成形方法
本专利技术涉及人造石纹理加工领域，特别是一种人造石板纹理的加工成形方法。
技术介绍
人造石英石是由90％以上的天然石英和10％左右的色料、树脂和其他调节粘结、固化等的添加剂组成。人造石英石是经过负压真空、高频振动成型，加温固化生产方法加工而成的板材。现有人造石英石技术中，要制造出类似天然石的纹理走向效果，需要在布料工序中放入纹理模框，布料结束后，将纹理模框移开，布出的料呈现出纹理线条，而此技术的缺点在于：1、一个纹理模框只能做出一种纹理线条效果，而要改变纹理线条，必须重新制造纹理模框；2、往纹理线条内填充色料只能依靠人工操作，无法实现生产自动化；3、纹理效果单一，无法实现多种色料组合渐变的纹理效果，与真实天然石的纹理效果差异很大。
技术实现思路
针对上述缺陷，本专利技术的目的在于提出一种人造石板纹理的加工成形方法。为达此目的，本专利技术采用以下技术方案：一种人造石板纹理的加工成形方法；包括以下步骤：a、布料，在产品模具内布施原料混合物，以得到具有板坯形状的板料；b、施加挤压力，向板料施加挤压力；c、布施色料，在板料的表面上布施至少一层色...
【技术保护点】
一种人造石板纹理的加工成形方法，其特征在于：包括以下步骤：a、布料，在产品模具内布施原料混合物，以得到具有板坯形状的板料；b、施加挤压力，向板料施加挤压力；c、布施色料，在板料的表面上布施至少一层色料，或者按照最终产品纹理的设计路径，在板料表面的对应位置均匀布施至少一层色料；d、层间搅拌，按照最终产品纹理的设定路线，在板料表面的所有对应位置或局部对应位置进行搅拌，且搅拌发生色料与原料混合物之间。
【技术特征摘要】
1.一种人造石板纹理的加工成形方法，其特征在于：包括以下步骤：a、布料，在产品模具内布施原料混合物，以得到具有板坯形状的板料；b、施加挤压力，向板料施加挤压力；c、布施色料，在板料的表面上布施至少一层色料，或者按照最终产品纹理的设计路径，在板料表面的对应位置均匀布施至少一层色料；d、层间搅拌，按照最终产品纹理的设定路线，在板料表面的所有对应位置或局部对应位置进行搅拌，且搅拌发生色料与原料混合物之间。2.根据权利要求1所述的加工成形方法，其特征在于：完成所述加工成形方法的各步骤之后，对得到的板料依次进行压制和固化。3.根据权利要求1所述的加工成形方法，其特征在于：步骤a和步骤b在同一工位上完成，步骤c和步骤d分别在相对独立的两个工位上...