The present invention provides a foamed polyethylene sheet, comprises the following components in parts by weight: 70 low density polyethylene 80, two azo formamide 15 21, two 3 cumene peroxide 5, isopropyl three (twelve alkyl sulfonyl titanate base) 0.3 1, stearic 5 acid 10, stearic acid zinc 2 Zinc Oxide 1 3 copies, 1.5 copies, 20 copies of the 15 plant fiber and inorganic filler 1 1.5. The foamed polyethylene sheet described in the invention has the characteristics of good material elasticity, good stereotyping and good environmental protection. The invention also provides the preparation method of the foamed polyethylene sheet, which is simple in operation, high in work efficiency and low in cost.
【技术实现步骤摘要】
一种发泡聚乙烯板材及其制备方法
本专利技术属于聚乙烯发泡材料
，特别是涉及一种发泡聚乙烯板材及其制备方法。
技术介绍
聚乙烯(PE)具有优良的物理、化学和力学性能，其韧性、挠曲性和缓冲性能好，具有电绝缘、隔热等特性，广泛应用于包装、化工和建筑等领域。PE发泡材料是最早工业化应用且应用较广的发泡材料之一。但是目前聚乙烯发泡材料仍存在弯曲强度、压缩强度和耐热性差，刚性和硬度低等不足，限制了它的应用。
技术实现思路
针对上述技术问题，本专利技术的目的在于提供一种具弹性好、定型性好的发泡聚乙烯薄膜，本专利技术还提供了所述发泡聚乙烯板材的制备方法。本专利技术采用的技术方案是：一种发泡聚乙烯板材，由如下重量份数的组分组成：低密度聚乙烯70-80份、偶氮二甲酰胺15-21份、过氧化二异丙苯3-5份，异丙基三(十二烷基苯磺酞基)钛酸酯0.3-1份，硬脂酸5-10份、硬脂酸锌2-3份，氧化锌1-1.5份，植物纤维15-20份和无机填料1-1.5份。本专利技术所述发泡聚乙烯板材，其中，所述无机填料为碳酸钙和滑石粉中一种或两种。本专利技术所述发泡聚乙烯板材，其中，由如下重量份数的组分...
【技术保护点】
一种发泡聚乙烯板材，其特征在于：由如下重量份数的组分组成：低密度聚乙烯70‑80份、偶氮二甲酰胺15‑21份、过氧化二异丙苯3‑5份，异丙基三(十二烷基苯磺酞基)钛酸酯0.3‑1份，硬脂酸5‑10份、硬脂酸锌2‑3份，氧化锌1‑1.5份，植物纤维15‑20份和无机填料1‑1.5份。
【技术特征摘要】
1.一种发泡聚乙烯板材，其特征在于：由如下重量份数的组分组成：低密度聚乙烯70-80份、偶氮二甲酰胺15-21份、过氧化二异丙苯3-5份，异丙基三(十二烷基苯磺酞基)钛酸酯0.3-1份，硬脂酸5-10份、硬脂酸锌2-3份，氧化锌1-1.5份，植物纤维15-20份和无机填料1-1.5份。2.根据权利要求1所述发泡聚乙烯板材，其特征在于：所述无机填料为碳酸钙和滑石粉中一种或两种。3.根据权利要求1所述发泡聚乙烯板材，其特征在于：由如下重量份数的组分组成：低密度聚乙烯80份、偶氮二甲酰胺16份、过氧化二异丙苯4份，异丙基三(十二烷基苯磺酞基)钛酸酯2份，硬脂酸10份、硬脂酸锌2份，氧化锌1.5份，植物纤维18份，碳酸钙0.5份和滑石粉1份。4.根据权利要求1-3任意一项所述发泡聚乙烯板材，其特征在于：所述植物纤维为竹纤维、甘蔗渣、秸秆、废纸和花椰菜中一种或几种。5.权利要...
【专利技术属性】
技术研发人员：汪锋，王龙珑，
申请(专利权)人：合肥朗胜新材料有限公司，
类型：发明
国别省市：安徽,34