The invention discloses a rubber mold, which comprises the following components: raw materials made of epoxy natural rubber 80 130 weight portions, 2 to 8 parts by weight of polychloroprene, Zinc Oxide 3 nano 7 weight portions, stearic acid 1 5 weight portions, 0.5 sulfur powder in 3 weight portions, 22 weight portions, 28 Black 9 to 12 parts by weight of aluminum phosphate, lignin 1 4 weight portions, carbon tetrachloride 2 5 weight portions, TBHQ 3 7 weight. The invention adopts epoxy natural rubber, polychloroprene, nano Zinc Oxide, stearic acid, sulfur powder, carbon black, aluminum phosphate, lignin, carbon tetrachloride, TBHQ and other raw materials made of rubber, the components interact with each other, the antiseptic effect is good, and has good corrosion resistance and heat resistance.
【技术实现步骤摘要】
一种防霉橡胶
本专利技术涉及橡胶
,具体涉及一种防霉橡胶。
技术介绍
天然橡胶属于天然高分子物质，其主要成分是聚异戊二烯，但仍含有少量的蛋白质、脂肪酸、糖分等有利于霉菌繁殖的物质，对微生物的敏感性较大，易受到霉菌的侵蚀。因此在天然橡胶加工生产过程中就必须考虑到防霉问题，这方面比较经典的例子就是在烟片胶的加工工艺中有熏烟工序，其目的是利用烟中所含的有机酸和酚类物质作防霉剂，避免生胶发霉。合成橡胶通常是不易受霉菌分割的但由于制品中往往加入了增塑剂、稳定剂、填充剂、润滑剂等加工助剂，尤其是增塑剂，这类物质对霉菌较敏感，致使合成橡胶制品也易受到霉菌侵蚀而破坏。一般来说，在橡胶制品加工过程中加入的增塑剂的分子量较低，如邻苯二甲酸酯类的分子量不超过400，它们会随着使用时间的延长由制品内部迁移到制品表面，特别是在温度高、湿度大、背阴等条件下更易受到霉菌、细菌的攻击，助长它们的繁殖，使制品的表面变色，产生斑点，甚至出现细孔，从而影响橡胶制品的正常作用。由于配合剂的使用对橡胶制品的质量影响很大，因而在防霉剂的选择应用时不仅要考虑到对霉菌的灭杀或抑制，还需要考虑高分子材料或其...
【技术保护点】
一种防霉橡胶，其特征在于由以下组分原料制成：环氧天然橡胶80‑130重量份、聚氯丁二烯2‑8重量份、纳米氧化锌3‑7重量份、硬脂酸1‑5重量份、硫磺粉末0.5‑3重量份、炭黑22‑28重量份、磷酸铝9‑12重量份、木质素1‑4重量份、四氯化碳2‑5重量份、特丁基对苯二酚3‑7重量份。
【技术特征摘要】
1.一种防霉橡胶，其特征在于由以下组分原料制成：环氧天然橡胶80-130重量份、聚氯丁二烯2-8重量份、纳米氧化锌3-7重量份、硬脂酸1-5重量份、硫磺粉末0.5-3重量份、炭黑22-28重量份、磷酸铝9-12重量份、木质素1-4重量份、四氯化碳2-5重量份、特丁基对苯二酚3-7重量份。2.根据权利要求1所述的防霉橡胶，其特征在于由以下组分原料制成：环氧天然橡胶90-120重量份、聚氯丁二烯4-6重量份、纳米氧化锌4-6重量份、硬...
【专利技术属性】