The invention discloses a novel preparation of graphene preparation method, including high pure graphite, the anionic surface active agent, dispersing agent, defoaming agent and solvent, stirring, mixing the slurry after drying and crushing, grinding particles by blowing mechanism will smash particles blow to gold wax alcohol, will stick with a mixture of crushed particles in cetyl alcohol and deionized water, heating and volatilization of cetyl alcohol, filtering and fast drying obtained graphene powder. The beneficial effect of the invention is that not only the production cost is saved, but also the production efficiency is high.
【技术实现步骤摘要】
石墨烯的新型制备方法
本专利技术涉及照明
，特别是石墨烯的新型制备方法。
技术介绍
锂离子电池的充放电过程就是Li+在正负极材料之间可逆地嵌入和脱嵌的过程。在充电时正极材料中的Li+脱离正极，进入电解液，通过隔膜向负极迁移，在负极上捕获电子而被还原，并贮存在层状结构材料中；放电时，负极中的锂会失去电子而形成Li+，进入电解液，穿过隔膜向正极方向迁移，并贮存在正极材料中。理想的锂离子电池应具有比容量高、密度大、能量密度高、安全性好、低温性能好、倍率性能佳、寿命长等品质，这就要求其正负极材料需具备比表面积大、导电性好、内阻小、电解液浸润性好等特点。碳基材料作为锂电池正负极材料而备受关注。现在使用的碳基材料有活性炭、活性炭纤维、炭气凝胶以及碳纳米管等，但上述的碳基材料由于达到的比容量不理想、纯度不够高或制备生产过程程序复杂、成本高而限制了其应用。石墨烯因其优异的电学性能、超高的比表面积、优良的化学稳定性和热力学稳定性而被认为是一种理想的锂离子电池电极材料。现在常见的石墨烯制备时，通常是将石墨烯粉末置于去离子水、或置于去离子水和乙醇的混合物中，通过搅拌或超声波的方法...
【技术保护点】
石墨烯的新型制备方法，其特征在于：它包括以下步骤：S1、混合，将高纯膨胀石墨、阴离子型有关表面活性剂、分散剂、消泡剂和溶剂置于反应釜中机械搅拌30~120min ，形成混合料浆；S2、粉碎，将上述混合料浆置于烘箱内进行烘干，烘干温度为100℃~150℃，烘干后形成固体，将上述固体进行粉碎，形成粒径小于100μm的粉碎颗粒；S3、铺放，在低温装置中，将形成平面的鲸蜡醇竖直放置，通过吹风机构将粉碎颗粒吹至金蜡醇面，一些粉碎颗粒粘在鲸蜡醇面上，而其他的粉碎颗粒掉落；S4、形成，将粘有粉碎颗粒的鲸蜡醇快速地从低温装置中取出，并将其置于去离子水和乙醇的混合物中，逐渐加热去离子水和乙醇...
【技术特征摘要】
1.石墨烯的新型制备方法，其特征在于：它包括以下步骤：S1、混合，将高纯膨胀石墨、阴离子型有关表面活性剂、分散剂、消泡剂和溶剂置于反应釜中机械搅拌30~120min，形成混合料浆；S2、粉碎，将上述混合料浆置于烘箱内进行烘干，烘干温度为100℃~150℃，烘干后形成固体，将上述固体进行粉碎，形成粒径小于100μm的粉碎颗粒；S3、铺放，在低温装置中，将形成平面的鲸蜡醇竖直放置，通过吹风机构将粉碎颗粒吹至金蜡醇面，一些粉碎颗粒粘在鲸蜡醇面上，而其他的粉碎颗粒掉落；S4、形成，将粘有粉碎颗粒的鲸蜡醇快速地从低温装置中取出，并将其置于去离子水和乙醇的混合物中，逐渐加热去离子水和...
【专利技术属性】
技术研发人员：刘兴翀，魏欣，魏泽忠，
申请(专利权)人：成都格莱飞科技股份有限公司，
类型：发明
国别省市：四川,51