The invention relates to a fluorescent type waterborne polyurethane slurry, which comprises the following components: 12 weight portions 20 aqueous polyurethane, 30 40 copies, 4 copies of 2 starch fluorescent agent, the aqueous polyurethane is composed of a mixture of toluene diisocyanate, polypropylene glycol and dimethylol propionic acid, quality the toluene diisocyanate, polypropylene glycol and dimethylol propionic acid ratio was 10:3:3. The waterborne polyurethane sizing slurry has good performance, easy desizing, biodegradation speed, no environmental pollution, also contain fluorescent agents, which can emit fluorescence in the dark environment, according to the different needs of application in construction industry work clothes dyeing, printing and dyeing can be used in all kinds of fire safety fabrics the.
【技术实现步骤摘要】
荧光型水性聚氨酯浆料
本专利技术涉及一种荧光型水性聚氨酯浆料,属于纺织工程
技术介绍
经纱上浆是织造的关键步骤之一,上浆效果的好坏直接决定了织造效率与织物质量,影响上浆效果的主要因素是浆料的上浆性能。随着人们对节能、环保意识的逐渐增强,对浆料的上浆性能提出了更高的要求。淀粉类水性聚氨酯浆料是一种再生资源,具有来源广泛、价格低廉及环境友好等特点,是目前广泛使用的浆纱材料。但现有的淀粉类水性聚氨酯浆料中往往会添加聚乙烯醇,聚乙烯醇纺织浆料具有优异的浆膜性能和良好的粘附性能,但聚乙烯醇属于高难度生物降解的有机物,存在退浆性能差和环境保护的问题。另外,纺织染料是用于纺织品染色的一种染剂,随着人们生活水平的日益提高,对不同纺织染料的需求也来越大,带有荧光的纺织染料日益受到人们的关注。
技术实现思路
本专利技术要解决技术问题是:克服上述技术的缺点,提供一种易于退浆、生物降解速度快且在黑暗环境下能发出荧光的荧光型水性聚氨酯浆料。为了解决上述技术问题,本专利技术提出的技术方案是:一种荧光型水性聚氨酯浆料,包括以下质量份数的各组分:12-20份水性聚氨酯、30-40份淀粉、2-4份荧光剂,所述水性聚氨酯是由甲苯二异氰酸酯、聚丙二元醇和二羟甲基丙酸组成的混合物,所述甲苯二异氰酸酯、聚丙二元醇和二羟甲基丙酸的质量比为10:3:3。本专利技术带来的有益效果是:本专利技术没有使用聚乙烯醇,而是采用水性聚氨酯,水性聚氨酯能够溶解或者分散到水中,对合成纤维具有较好的黏合强度,与亲水性纤维具有很好的粘着性能。其中二羟甲基丙酸可以提高浆膜的断裂强度、吸水性能,而聚丙二元醇可以提高分子 ...
【技术保护点】
一种荧光型水性聚氨酯浆料,其特征在于,包括以下质量份数的各组分:12‑20份水性聚氨酯、30‑40份淀粉、2‑4份荧光剂,所述水性聚氨酯是由甲苯二异氰酸酯、聚丙二元醇和二羟甲基丙酸组成的混合物,所述甲苯二异氰酸酯、聚丙二元醇和二羟甲基丙酸的质量比为10:3:3。
【技术特征摘要】
1.一种荧光型水性聚氨酯浆料,其特征在于,包括以下质量份数的各组分:12-20份水性聚氨酯、30-40份淀粉、2-4份荧光剂,所述水性聚氨酯是由甲苯二异氰酸酯、聚丙二元醇和二羟...