The present invention relates to a kind of coating, in particular to a waterproof coating with multi wall carbon nanotubes. The device consists of the following components, its composition and weight: 20 emulsion powder 20 45 copies, 30 copies, 3 copies of 1 calcium carbonate masterbatch, 3 activity of 5 copies, 5 copies of antioxidant 3, defoaming agent 1 3 copies, 3 5 titanium dioxide 8 copies, 10 copies of polyvinyl alcohol, Portland 3 5 copies, 15 copies of 13 quartz sand, water 10. The invention has the advantages of waterproof, anti steam, strong adhesion, good film-forming hardness; adding anti-aging agent and defoaming agent, easy foaming, anti mildew, anti aging; PVA thickening effect.
【技术实现步骤摘要】
一种含多壁碳纳米管的防水涂料
本专利技术涉及一种涂料,具体涉及一种含多壁碳纳米管的防水涂料。
技术介绍
内外墙的涂料品种较多,尤其是高分子乳液材料的出现,为涂料的品种增添了许多新品种。其防水、抗氧化能力增强。然而,现有的含多壁碳纳米管的防水涂料不能长期有效地防雨水、抗冲刷。因此,经常看到装饰和涂刷整洁美观的建筑物经不住风雨冲刷和湿气浸蚀而色彩斑驳。主要是这些涂料中缺少化学性能稳定、不溶于水的无机物质,涂料性能与建筑物本体物理性能不相近。因而,其综合防水性能效果不佳,易老化。
技术实现思路
本专利技术为了克服现有涂料的缺点,提供一种含多壁碳纳米管的防水涂料。本专利技术的技术方案是:一种含多壁碳纳米管的防水涂料,其特征在于由以下成分组成,其成分和重量份数为:苯丙乳液20-45份,多壁碳纳米管0.5-2份,石粉20-30份,碳酸钙1-3份,活性母料3-5份。本专利技术所述的苯丙乳液为苯乙烯、丙烯酸脂共聚乳液,或者是苯乙烯、丙烯酸脂和丙烯酸共聚乳液。所述的含多壁碳纳米管的防水涂料还包括木质素磺酸盐1-5份、硬脂酸钙2-4份。所述的含多壁碳纳米管的防水涂料还包括防老剂3-5份,消泡剂1-3份,钛白粉3-5份,聚乙烯醇8-10份,硅酸盐3-5份,石英砂13-15份。一种含多壁碳纳米管的防水涂料的制备方法,由以下步骤构成:将各成分按比例逐步混合,一边加入,一边搅拌,使其混合均匀,最后再加入水充分混合均匀,即成为含多壁碳纳米管的防水涂料。涂料一般在5℃以上即可成膜,温度越高,成膜更有利。在粉刷涂料时,一般情况下粉刷一层就够,厚度为0.1-2mm,如果想增强防水效果,也可以多刷 ...
【技术保护点】
一种含多壁碳纳米管的防水涂料,其特征在于:由以下成分组成,其成分和重量份数为:苯丙乳液20‑45份,多壁碳纳米管0.5‑2份,石粉20‑30份,碳酸钙1‑3份,活性母料3‑5份。
【技术特征摘要】
1.一种含多壁碳纳米管的防水涂料,其特征在于:由以下成分组成,其成分和重量份数为:苯丙乳液20-45份,多壁碳纳米管0.5-2份,石粉20-30份,碳酸钙1-3份,活性母料3-5份。2.根据权利要求1所述的一种含多壁碳纳米管的防水涂料,其特征在于:所述的苯丙乳液为苯乙烯、丙烯酸脂共聚乳液,或者是苯乙烯、丙烯酸脂和丙烯酸共聚乳液。3.根据权...
【专利技术属性】
技术研发人员:吕世宁,
申请(专利权)人:山东蓝盟防腐科技股份有限公司,
类型:发明
国别省市:山东,37