The invention discloses a method for preparing activated carbon from waste circuit board. The method for non metal parts of the waste circuit board is broken into powder with ammonium nitrate solution, and then centrifuged at the top of the resin and the resin, epoxy curing agent, the resin cured carbide carbide, the carbide prepared activated carbon activated. By pretreating the waste metal powder of the circuit board, the invention can extract the resin part for preparing the activated carbon, thereby removing other impurities, improving the preparation efficiency of the activated carbon and reducing the energy consumption, and has great application prospects.
【技术实现步骤摘要】
一种利用废电路板制备活性炭的方法
本专利技术属于固体废弃物处理
更具体地，涉及一种利用废电路板制备活性炭的方法。
技术介绍
由于科技日新月异的发展，电子垃圾以迅猛的速度飞快增长，对环境和人类健康都造成了巨大的威胁。在电子垃圾中，废电路板占据着较大的比重，且其内所含金属资源与矿藏相媲美。目前，对于废电路板的回收利用多集中在废电路板的金属部分的回收利用工艺，且部分技术已经相当成熟。但是，相比金属部分而言，非金属部分在废电路板中占据更大的比重，因此，开发利用废电路板的非金属部分对于电子垃圾的回收利用具有重大意义。专利文献CN101948110A，CN102923702A，CN104591182A和CN104591183A均公开了以废旧印刷电路板制备活性炭，通过直接将非金属部分粉碎成粉末后进行活性炭制备，由于电路板的非金属部分含有树脂、玻璃纤维以及少量金属等，杂质的存在会使活性炭的制备效率低下，产量不高，且杂质会对活性炭的品质造成影响。
技术实现思路
本专利技术所要解决的技术问题是克服现有利用废电路板制备活性炭的缺陷和不足。通过对废电路板非金属粉末进行预处理，分选出用...
【技术保护点】
一种利用废电路板制备活性炭的方法，其特征在于，将废电路板的非金属部分破碎成粉末后用硝酸铵溶液浸泡处理，再离心得到最上部的树脂，然后将树脂用环氧固化剂固化，再将固化后的树脂碳化得到碳化物，最后将碳化物活化制备得到活性炭。
【技术特征摘要】
1.一种利用废电路板制备活性炭的方法，其特征在于，将废电路板的非金属部分破碎成粉末后用硝酸铵溶液浸泡处理，再离心得到最上部的树脂，然后将树脂用环氧固化剂固化，再将固化后的树脂碳化得到碳化物，最后将碳化物活化制备得到活性炭。2.根据权利要求1所述的方法，其特征在于，所述硝酸铵溶液的质量浓度为43%～67%。3.根据权利要去1所述的方法，其特征在于，所述硝酸铵溶液与非金属粉末的质量比为1：0.2～1。4.根据权利要去1所述的方法，其特征在于，所述离心为5000转/分离心10～20分钟。5.根据权利要求1所述的方法，其特征在于，所述树脂与环氧固...
【专利技术属性】
技术研发人员：韦献革，杜长明，阮菊俊，周小琳，熊亚，仇荣亮，
申请(专利权)人：中山大学，
类型：发明
国别省市：广东,44