一种单组分聚氨酯防水涂料及其制备方法技术

本发明专利技术公开了一种单组分聚氨酯防水涂料及其制备方法，该涂料以甲苯二异氰酸酯、聚醚多元醇DL和828为主要原料，制备方法简单，可控性强，生产过程中污染物排放少，易于工业化生产和推广应用；同时产品性能好，不仅具有优异的物理机械性能，还具有较好的耐热性、耐酸碱性以及抗老化等性能，可将其应用于多种环境，适用性广，具有很好的市场前景。

A single component polyurethane waterproof coating and its preparation method

The invention discloses a single component polyurethane waterproof paint and preparation method of the coating by toluene diisocyanate, polyether polyol and DL 828 as the main raw material, the preparation method is simple, controllable, less pollutant emissions in the production process, easy industrial production and application; at the same time, product performance is good, not only has the physical excellent mechanical properties, but also has good heat resistance, acid and alkali resistance and anti-aging properties, which can be used in a variety of environments, wide applicability, and has good market prospects.

【技术实现步骤摘要】
一种单组分聚氨酯防水涂料及其制备方法
本专利技术涉及涂料领域，具体涉及一种单组分聚氨酯防水涂料及其制备方法。
技术介绍
随着城市化进程开展，城市用水体系也随之发展。城市住宅区供水贮存时间长、条件差，经常会在箱体出现异味、铁锈、藻类、红虫等现象，引起水质恶化，造成二次供水安全隐患。因此通过必要的手段保证供水设施的安全是必要的途径。防水涂料作为一种新型功能高分子材料，可作为自来水管道、贮水池等供水设施内壁上的内衬防护涂料，是一种有效的方式。但对材料有较高的要求，包括良好附着力、无毒、耐洗刷、耐老化及防水防渗等性能，因此研制一种高性能防水涂料很有必要。聚氨酯防水涂料素有“液体橡胶”的美誉，具有物理性能良好，防水效果优，施工维修方便，使用寿命长等优点，可适用于建筑物的防水防潮甚至堵漏。目前现有的聚氨酯防水涂料主要分为沥青聚氨酯、单组分聚氨酯、双组份聚醚型聚氨酯防水涂料以及彩色聚氨酯防水涂料。其中应用最广泛的是单组分聚氨酯防水涂料，单组分聚氨酯防水涂料的聚合物相对分子质量较大，成膜过程中一般发生交联，但是其生产制备过程常需要在真空环境或氮气保护下进行，导致生产步骤繁琐，如中国专利CN10487本文档来自技高网...

【技术保护点】
一种单组分聚氨酯防水涂料，其特征在于，按重量份计，组份含量包括：

【技术特征摘要】
1.一种单组分聚氨酯防水涂料，其特征在于，按重量份计，组份含量包括：2.权利要求1中所述的一种单组分聚氨酯防水涂料的制备方法，其特征在于，步骤如下：1)将原料聚醚GEP-828加入到反应釜中，开始搅拌后加入聚醚DL，改性树脂，以及催化剂，升温至40～55℃；2)继续搅拌15～30min后，加入TDI及苯甲酰氯，继续升温至70～80℃反应2～3h；3)加入各种填料、颜料、分散剂及溶剂油等，搅拌并反应1h；4)降低温度至50℃以下，加入防老剂、消泡剂，搅拌1～2h，检测合格后出料。3.根据权利要求2所述的一种单组分聚氨酯防水涂料的制备方法，其特征在于，步骤3)中所述的催化剂为二月...