The present invention relates to the technical field of footwear, particularly a high wear-resistant rubber shoes, which is composed of 2 3 parts by weight of polyethylene wax, 10 20 weight naphthenic oil, 5 15 weight metallocene catalyzed polyolefin, 10 25 weight portions of amorphous poly alpha olefin, 5 15 weight ethylene hydrogenation isoprene styrene copolymer, 5 10 weight portions of tackifying resin, 5 10 weight phenolic terpene resin, 3 8 weight portions of hydrogenated C5 petroleum resin, 1 3 weight polyisobutylene, 1 2 weight portions of adipic acid two ester, 0.8 1.5 weight and 0.5 antioxidants 1.5 weight coupling agent. A kind of high wear-resisting rubber shoes produced by the invention, the design formula and the reasonable dosage, can greatly improve the wear resistance of rubber shoes, in order to prepare the shoes soles wear resistance improved greatly, prolong the service life of the shoes, improve service performance.
【技术实现步骤摘要】
一种高耐磨鞋胶
本专利技术涉及制鞋
，尤其是一种高耐磨鞋胶。
技术介绍
现有技术中，对于鞋底用胶料的要求越来越高，由于对于其耐磨性能，其高耐磨性能决定了其使用寿命及使用性能。现有市面上的鞋底所采用的鞋胶都存在耐磨性能差等缺点。
技术实现思路
本专利技术的目的是为了解决上述技术的不足而提供一种耐磨性能优越而提升了鞋底的使用寿命的高耐磨鞋胶。为了达到上述目的，本专利技术所设计的一种高耐磨鞋胶，它由2-3重量份聚乙烯蜡，10-20重量份环烷油，5-15重量份茂金属催化聚烯烃，10-25重量份无定型聚-α-烯烃，5-15重量份氢化乙烯-异戊二烯-苯乙烯共聚物，5-10重量份增粘树脂，5-10重量份酚醛-萜烯树脂，3-8重量份加氢C5石油树脂，1-3重量份聚异丁烯，1-2重量份已二酸二辛酯，0.8-1.5重量份抗氧化剂和0.5-1.5重量份偶联剂组成。本专利技术所得到的一种高耐磨鞋胶，其通过合理的配方及用量的设计，能极大的提升了鞋胶的耐磨性能，从而在制备成鞋子后鞋底的耐磨性极大的提升，延长了鞋子的使用寿命，提升使用性能。具体实施方式下面通过实施例对本专利技术作进一步的描述。实施例1：本实施例描述的一种高耐磨鞋胶，它由2重量份聚乙烯蜡，10重量份环烷油，5重量份茂金属催化聚烯烃，10重量份无定型聚-α-烯烃，5重量份氢化乙烯-异戊二烯-苯乙烯共聚物，5重量份增粘树脂，5重量份酚醛-萜烯树脂，3重量份加氢C5石油树脂，1重量份聚异丁烯，1重量份已二酸二辛酯，0.8重量份抗氧化剂和0.5重量份偶联剂组成。实施例2：本实施例描述的一种高耐磨鞋胶，它由3重量份聚乙烯蜡，20...
【技术保护点】
一种高耐磨鞋胶，其特征是：它由2‑3重量份聚乙烯蜡，10‑20重量份环烷油，5‑15重量份茂金属催化聚烯烃，10‑25重量份无定型聚‑α‑烯烃，5‑15重量份氢化乙烯‑异戊二烯‑苯乙烯共聚物，5‑10重量份增粘树脂，5‑10重量份酚醛‑萜烯树脂，3‑8重量份加氢C5石油树脂，1‑3重量份聚异丁烯，1‑2重量份已二酸二辛酯，0.8‑1.5重量份抗氧化剂和0.5‑1.5重量份偶联剂组成。
【技术特征摘要】
1.一种高耐磨鞋胶，其特征是：它由2-3重量份聚乙烯蜡，10-20重量份环烷油，5-15重量份茂金属催化聚烯烃，10-25重量份无定型聚-α-烯烃，5-15重量份氢化乙烯-异戊二烯-苯乙烯共聚物...