一种T／P91耐热钢加速老化方法技术
An accelerated aging method for T / P91 heat-resistant steel
The invention relates to the field of heat treatment of steel materials, in particular to a heat treatment method for accelerating aging of T/P91 heat-resistant steel. First, high temperature short matrix carbide accelerated aging, aging with AC1 below the temperature of 20 DEG C; complete aging reaging under 620 degrees, in order to ensure the rapid aging of Laves phase, and ultimately equivalent to the actual condition of organization under different periods. The accelerated aging method provided by this invention can quickly get different aging organizations of T/P91 heat-resistant steel. By comparing the accelerated aging tissue with the actual working conditions, the accelerated aging test of this invention achieves accurate and reliable equivalent simulation effect. Thus, it solves the technical problem that the existing T/P91 technology is short in service time, and can not get different aging organizations at all stages of operation, and can not effectively evaluate the aging level.
【技术实现步骤摘要】
一种T/P91耐热钢加速老化方法
本专利技术涉及钢铁材料的热处理领域，特别涉及一种T/P91耐热钢加速老化的热处理方法。
技术介绍
新型马氏体耐热钢组织中的析出相主要有MX类碳氮化物、M23C6型碳化物，以及在高温长时(500小时以上)大量析出的Laves相，而Z相则要在几万小时长时高温服役后才会出现。在这4种重要的析出相中，MX类碳氮化物和M23C6型碳化物热稳定性较好，其中MX类碳氮化物最为稳定，几万小时长时高温服役后依然不发生明显长大。M23C6型碳化物热稳定性稍差，但其长大符合奥斯瓦尔德熟化规律；Laves相在服役一段时间析出后，其长大也符合奥斯瓦尔德熟化规律；Z相的形成是通过氮化物析出相逐步演变而形成的，其长大过程也符合奥斯瓦尔德熟化规律。在钢中析出相的析出长大和回溶于基体两个过程同时存在，在某一固定温度下，两个过程共同作用的最终状态就是热力学的平衡态。T/P91耐热钢中Fe2Mo型Laves相虽然在长时高温服役后长大迅速并对蠕变性能产生影响，但是它在钢中的全固溶温度就在700℃度左右，也就是说，如果老化加速实验只是将时效温度提高到700℃，将不会得到L...
【技术保护点】
一种T/P91耐热钢加速老化方法，其特征在于，首先进行基体、碳化物的高温快速短时加速老化，选用AC1点以下20～30℃的温度下进行时效，时间为0～800h；老化完成再在620℃下时效，以保证快速析出Laves相，最终实现等效于实际工况不同时期下的老化组织。
【技术特征摘要】
1.一种T/P91耐热钢加速老化方法，其特征在于，首先进行基体、碳化物的高温快速短时加速老化，选用AC1点以下20～30℃的温度下进行时效，时间为0～800h；老化完成再在620℃下时效，以保证快速析出Laves相，最终实现等效于实际工况...
【专利技术属性】
技术研发人员：严伟，杨旭，单以银，肖福仁，杨柯，
申请(专利权)人：中国科学院金属研究所，
类型：发明
国别省市：辽宁,21