The present invention relates to a cement grinding agent field, especially relates to a high grinding temperature of cement grinding agent and a preparation method thereof, which is characterized in that, according to the quality of copies, including 30~60 copies of aliphatic sulfonic acid sodium and aluminum sulfate mixed solution, 1~10 copies of three hydroxyethyl amine, 5~10 copies, 1~10 copies of alcamines sodium tripolyphosphate, sodium gluconate, 1~10 copies of the 0.1 to 5 copies, 10~30 copies of the water dispersing agent. The invention can reduce the material surface energy, weaken the agglomeration effect produced by molecular attraction, help to accelerate the expansion of external work when particles crack, to improve the grinding efficiency, achieve the purpose of energy saving, high yield and high quality, the ball mill, can reduce the cement fineness and improving mill output table.
【技术实现步骤摘要】
一种高磨温水泥助磨剂及其制备方法
本专利技术属于水泥粉磨
，尤其涉及一种高磨温水泥助磨剂及其制备方法。。
技术介绍
在水泥粉磨时加入的起助磨作用而又不损害人体健康和水泥混凝土性能的外加剂，称为助磨剂，分为粉体和液体两种。它是一种改善水泥粉磨效果和性能的化学添加剂，适量地加入到被粉磨的物料中，能通过它对颗粒表面的物理化学作用，可以显著提高水泥台时产量、各龄期水泥强度，改善其流动性。助磨剂应用于水泥生产，可降低熟料用量，多消耗工业废渣，降低水泥粉磨电耗，在节能减排方面的效果显著；我国是水泥大国，如有60%的水泥企业应用助磨剂，则可节电81亿Kwh以上，节煤850万吨以上，减少CO2、SO2有害气体的排放量等。现有技术中，在磨机中增加的传统水泥助磨剂中的醇胺类化合物易挥发及变质，严重影响助磨剂的使用性能，降低磨机的粉磨效率，使水泥物料的易磨性下降，磨机的粉磨效率下降，这是由于普通液体助磨剂主要含有三乙醇胺、聚合多元醇、聚合醇胺、三乙丙醇胺、乙二醇、丙二醇、丙三醇、脂肪酸钠、氯化钙、氯化钠、醋酸钠、硫酸铝、甲酸钙、木钙、木钠等。物料的易磨性随温度的升高而下降引起的，...
【技术保护点】
一种高磨温水泥助磨剂，其特征在于，按质量份数计，包括30～60份的脂肪族磺酸钠和硫酸铝的混合溶液、1～10份的三羟乙基胺、5～10份的醇胺类、1～10份的三聚磷酸钠、1～10份的葡萄糖酸钠、0.1～5份的分散剂、10～30份的水。
【技术特征摘要】
1.一种高磨温水泥助磨剂，其特征在于，按质量份数计，包括30～60份的脂肪族磺酸钠和硫酸铝的混合溶液、1～10份的三羟乙基胺、5～10份的醇胺类、1～10份的三聚磷酸钠、1～10份的葡萄糖酸钠、0.1～5份的分散剂、10～30份的水。2.如权利要求1所述一种高磨温水泥助磨剂，其特征在于，所述的脂肪族磺酸钠是碳数为14～18个碳原子的直链脂肪族烷基磺酸钠，所述的醇胺类物质为聚乙二醇、三乙醇...
【专利技术属性】
技术研发人员：徐建，谢昊，康慧芬，
申请(专利权)人：宁夏宝塔化工中心实验室有限公司，
类型：发明
国别省市：宁夏,64