一种新型高分子环保固沙剂及其制备方法技术

本发明专利技术公开了一种新型高分子环保固沙剂，按重量百分比组成为：聚乙烯醇8%‑20%、尿素5%‑15%、硼砂1%‑5%、可溶性淀粉5%‑20%、1%‑3%pH调节剂、5%‑20%有机酯、1%‑10%复合乳化剂、余量水。本发明专利技术的一种新型高分子环保固沙剂不仅可以起到固沙和吸湿保水效果，同时具有生物降解性能，黏度大，稀释后喷洒使用方便，与生物固沙结合使用效果更佳。

A New Polymer Environmental Protection Sand Fixing Agent and Its Preparation Method

The invention discloses a new macromolecule environmental protection sand fixing agent, which is composed of 8%-20% polyvinyl alcohol, 5%-15% urea, 1%-5% borax, 5%-20% soluble starch, 1%-3% pH regulator, 5%-20% organic ester, 1%-10% compound emulsifier and residual water according to weight percentage. The novel macromolecule environmental protection sand fixing agent of the invention not only has the effects of sand fixation, moisture absorption and water retention, but also has the characteristics of biodegradability, high viscosity, convenient spraying after dilution and use, and better combined use effect with biological sand fixing.

【技术实现步骤摘要】
一种新型高分子环保固沙剂及其制备方法
本专利技术属于化学固沙领域，具体涉及一种可降解的新型高分子环保固沙剂及其制备方法。
技术介绍
由于气候的变化、人口的增长、植被的破坏等外界因素的影响，使得土地承受的压力过于沉重，土地荒漠化日益严重。因此有效的预防和治理沙漠化是当今世界急需解决的问题，而廉价、高效且环保的防沙治沙材料则成为人们关注的热点。防沙治沙的主要的方式方法有：工程固沙、生物固沙、化学固沙和生物-化学-工程综合固沙。目前研究最多的就是化学固沙，化学固沙剂可以通过扩散的作用将固沙剂渗入到沙质地中，并且与沙粒粘黏在一起，在沙体表面形成一层固结层即保护膜。而用高分子聚合物来治理流沙和沙质地表，可以使分散的、不定形的沙粒粘黏成为体积大的具有一定韧性且不容易被破坏的稳定体，从而达到控制和改善沙害环境，提高沙地生产力的目的。
技术实现思路
本专利技术提供了一种新型的可降解的高分子环保固沙剂及其制备方法，该固沙剂具有水溶性好、黏度大、固沙和抗侵蚀效果优良、吸湿保水性好、成本低、可降解等特点，稀释后喷洒使用方便，使用前景可观。本专利技术的配方如下：按质量百分比计，包括：聚乙烯醇8%-20%、尿素5本文档来自技高网...

【技术保护点】
1.一种新型高分子环保固沙剂，其组成的重量百分比为：聚乙烯醇8%‑20%、尿素5%‑15%、硼砂1%‑5%、可溶性淀粉5%‑20%、1%‑3%pH调节剂、5%‑20%有机酯、1%‑10%复合乳化剂、余量水。