多孔片状钴/碳复合吸波材料及其制备方法技术
Porous sheet cobalt / carbon composite absorbing materials and their preparation methods
The invention relates to the field of absorption wave technology, in particular to a porous sheet cobalt / carbon composite absorbing material and a preparation method. The composite absorbing material includes a matrix, the matrix of porous structure and the pore size of 10 200nm hole is arranged in the carbon layer, the porosity is 5% 25%. The preparation method requires fewer reagents, simple preparation process, and no need for high-precision equipment assistance. The Co / C composite absorbing material obtained is porous flake structure, and the absorbing property of the composite can be adjusted by changing the content of glucose.
【技术实现步骤摘要】
多孔片状钴/碳复合吸波材料及其制备方法
本专利技术涉及吸波
，具体涉及一种多孔片状钴/碳复合吸波材料及其制备方法。
技术介绍
随着信息技术的不断发展，越来越多的高频电子设备逐渐出现在人们的日常生活中，随之带来的电磁波辐射不仅影响其他电子设备的正常运行，而且会对人体健康造成严重危害。如何有效地吸收电磁波辐射成为了一个亟需解决的难题。目前，电磁吸波材料按其损耗机理可分为磁损耗、介电损耗和电阻损耗三类。单一类型的吸波材料因其阻抗匹配失衡导致吸收效果较差，因此，制备包含两种或三种损耗机理的复合型吸波材料成为了研究趋势。磁性钴类吸波材料(钴粉、羰基钴等)因其吸收效果较强，原料来源广泛且价格低廉等优点一直受到研究者的广泛关注，其缺陷在于材料密度较大，有效吸收频宽（反射损耗<−10dB）较窄。为降低钴类吸波材料密度，拓展其吸波频宽，引入碳系材料与其复合是一种行之有效的途径。中国专利CN101728045A公开了一种氧化钴/碳复合纳米吸波材料的制备方法，该专利以有机溶剂为碳源，将非晶碳包覆在氧化钴内核上制备得到氧化钴/碳复合纳米吸波材料，该专利的技术方案对吸波...
【技术保护点】
一种多孔片状钴/碳复合吸波材料，其特征在于，所述复合吸波材料为多孔片状结构，包括片状的基体，基体内部为多孔结构，基体为钴/碳复合物，孔径为10‑200nm，孔内填充有碳层，孔隙率为5%‑25%。
【技术特征摘要】
1.一种多孔片状钴/碳复合吸波材料，其特征在于，所述复合吸波材料为多孔片状结构，包括片状的基体，基体内部为多孔结构，基体为钴/碳复合物，孔径为10-200nm，孔内填充有碳层，孔隙率为5%-25%。2.一种如权利要求1所述的多孔片状钴/碳复合吸波材料的制备方法，其特征在于，具体包括以下步骤：（1）将钴盐和尿素按照1:2-3的质量比溶于水中，并将混合液置于反应釜中反应12h以上，反应温度为120-125℃，反应结束后，进行抽滤，得到红棕色钴前驱体；（2）将上述得到的钴前驱体分散于浓度为0.14-0.42mol/L的葡萄糖溶液中，搅拌得到均匀的混合液；（3）步骤（2）得到的混合溶液在60℃下干燥24h得到钴前驱体/葡萄糖混合粉末；（4）将混合粉末在惰性气体氛围中进行热处理最终得到多孔片状钴/碳复合吸波材料。3.根据权利要求2所述的多孔片状钴/碳复合吸波材料的制备方法，其特征在于，所述钴盐为硫酸钴(CoSO4.7H2O)、硝酸钴中的一种。4.根据权利要求2所述的一种多孔片状钴/碳...
【专利技术属性】
技术研发人员：俞璐军，朱曜峰，董余兵，傅雅琴，
申请(专利权)人：浙江理工大学，
类型：发明
国别省市：浙江,33