The invention discloses a high strength anti alkali metal pipe and its preparation method, composition by weight percent: Mo1.5 ~ 2%, Cr1.5 ~ 2.30%, C0.4 ~ 0.5%, Cu = 0.6%, Ni = 0.6%, Si = 0.2%, Mn0.5 ~ 0.7%, P = 0.01%, S = 0.01%, N = 0.01% Al = 0.03%, Mg = 0.03%, Ca = 0.03%, B0.01 ~ 0.02%, Nb 0.01 ~ 0.06%, As = 0.01%, Sn = 0.01%, the balance of iron. The raw materials of iron smelting, refining and vacuum degassing, continuous casting billet, rolling circle controlled light pipe, tube after quenching and tempering heat treatment of light pipe. The pipe made by the invention can adapt to the use in saline alkali environment, has strong corrosion resistance and is not easy to corrode and damage, and ensures the normal transformation and planting and production of saline alkali soil, and avoids waste.
【技术实现步骤摘要】
高强度抗盐碱金属管材及其制备方法
本专利技术涉及一种属于防腐金属管及其制造方法，尤其涉及一种高强度抗盐碱金属管材及其制备方法。
技术介绍
在盐碱地的改造和种植生产中，会不可避免的用到金属管道。在使用中因这些金属管道会受到各种碱和盐离子的腐蚀而进入管体中，在应力作用下会发生腐蚀、开裂，导致金属管道受损，而影响管抗腐蚀因素主要有：管的硬度、组织和管化学成分。目前盐碱地改造和种植生产中所用到的金属管的硬度、组织和管化学成分大多不能适应盐碱环境下使用，造成金属管的大量腐蚀受损而损坏，不仅影响了盐碱地的改造和种植生产，也造成了大量的浪费。
技术实现思路
本专利技术所要解决的技术问题是：提供了一种能够适应在盐碱环境下使用，抗腐蚀性强，不易腐蚀受损，保证了盐碱地的正常改造和种植生产，避免了浪费的高强度抗盐碱金属管材。本专利技术还提供了一种高强度抗盐碱金属管材的制备方法。为解决上述技术问题，本专利技术的技术方案是：高强度抗盐碱金属管材，其特征在于管成分以重量％计为：Mo1.5～2％，Cr1.5～2.30％，C0.4～0.5％，Cu≤0.6％，Ni≤0.6％，Si≤0.2％，Mn0.5...
【技术保护点】
高强度抗盐碱金属管材，其特征在于管成分以重量％计为：Mo1.5～2％，Cr1.5～2.30％，C0.4～0.5％，Cu≤0.6％，Ni≤0.6％，Si≤0.2％，Mn0.5～0.7％，P≤0.01％，S≤0.01％，N≤0.01％，Al≤0.03％，Mg≤0.03％,Ca≤0.03％,B0.01～0.02％，Nb 0.01～0.06％，As≤0.01％，Sn≤0.01％，余量为铁。
【技术特征摘要】
1.高强度抗盐碱金属管材，其特征在于管成分以重量％计为：Mo1.5～2％，Cr1.5～2.30％，C0.4～0.5％，Cu≤0.6％，Ni≤0.6％，Si≤0.2％，Mn0.5～0.7％，P≤0.01％，S≤0.01％，N≤0.01％，Al≤0.03％，Mg≤0.03％,Ca≤0.03％,B0.01～0.02％，Nb0.01～0.06％，As≤0.01％，Sn≤0.01％，余量为铁。2.如权利要求1所述的高强度抗盐碱金属管材，其特征在于：管的屈服强度≥880Mpa。3.如权利要求1所述的高强度抗盐碱金属管材的制备方法，其特征在于,包括步骤：1)、将原料铁采用氧气转炉进行冶炼，采用炉外精炼...
【专利技术属性】
技术研发人员：王胜，
申请(专利权)人：潍坊友容实业有限公司，
类型：发明
国别省市：山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。