The invention discloses a high nitrogen martensitic stainless steel and its heat treatment method, high nitrogen martensitic stainless steel in weight percentage: C: < 0.03%, N:0.15 ~ 0.4%, Ni:1 ~ 3%, Mo:0.5 ~ 2%, Cr:10.5 ~ 14%, Mn:1 ~ 2.5%, Si:1 ~ 2%, P: < 0.005%, S: < 0.01%, Nb: < 0.2%, Ti: < 0.2%, the residual Fe and inevitable impurities. The invention of high nitrogen martensitic stainless steel and its heat treatment method, the carbon content control in ultra low range, reduce the high carbon materials for plastic toughness, alloy elements with scientific adding proportion reached more excellent performance, which can meet the strength and has good plasticity, toughness and corrosion resistance, and reduce the nickel content of 50%, to achieve high performance and low cost high nitrogen martensitic stainless steel.
【技术实现步骤摘要】
一种高氮马氏体不锈钢及其热处理方法
本专利技术涉及材料
，特别涉及一种高氮马氏体不锈钢及其热处理方法。
技术介绍
在天然石油气开采中，随着开采环境的日趋恶劣，使得开采设备的要求越来越高。面对井下的高温、高压、含高浓度CO2、少量H2S或Cl－的共存腐蚀环境，一般的标准井下套管在这种复杂的井下环境长时间工作，易于发生腐蚀、开裂，使用寿命降低甚至于出现井下套筒断裂的情况，无法满足现在所面临的环境。我国目前的大容量石油井田大多集中在西部高原地带，因此开采深度成为第一个需要面对问题。深井或超深井在开采中不仅承受着钻井过程中的拉力，同时还有地层带来的扭转力。所以急切需要强度、韧度更为优越的井下套筒材料。传统马氏体不锈钢(1Cr13、2Cr13、3Cr13等)属于高碳马氏体不锈钢，虽然具有良好的力学性能，能满足一般油气井用套管和油管所要求的强度。但其塑性和韧性指标相对较低，不能达到深井、超深井中所要求不低于759MPa的屈服强度，从而在管道作业循环中常出现破裂造成意外事故。因此不适宜用于深井、超深井井下钻套筒使用。目前，对传统马氏体不锈钢进行合金化是提高其综合力学性能的...
【技术保护点】
一种高氮马氏体不锈钢，其特征在于，按质量百分比计包括：C:＜0.03％，N:0.15～0.4％，Ni:1～3％，Mo:0.5～2％，Cr:10.5～14％，Mn:1～2.5％，Si:1～2％，P:＜0.005％，S:＜0.01％，Nb:＜0.2％，Ti:＜0.2％，剩余为Fe和不可避免杂质。
【技术特征摘要】
1.一种高氮马氏体不锈钢，其特征在于，按质量百分比计包括：C:＜0.03％，N:0.15～0.4％，Ni:1～3％，Mo:0.5～2％，Cr:10.5～14％，Mn:1～2.5％，Si:1～2％，P:＜0.005％，S:＜0.01％，Nb:＜0.2％，Ti:＜0.2％，剩余为Fe和不可避免杂质。2.如权利要求1所述的高氮马氏体不锈钢，其特征在于，按质量百分比计包括：C:＜0.01％，N:0.25～0.35％，Ni:1.5～2.5％，Mo:1～1.6％，Cr:11.5～13.5％，Mn:1.6～2.2％，Si:1.4～1.8％，P:＜0.005％，S:＜0.01％，Nb:0.1～0.15％，...
【专利技术属性】
技术研发人员：韩英，孙加岐，袁方兴，孙世成，陈华，冉旭，
申请(专利权)人：长春工业大学，
类型：发明
国别省市：吉林,22