一种节能环保材料制造技术

本发明专利技术公开了一种节能环保材料，由以下组分制成：海泡石、硅藻土、玻璃微珠、高岭土、珍珠岩、生石灰、成核剂、阻燃剂、聚甲基丙烯酸甲酯。所述组分的重量分数分别为：海泡石18～20份、硅藻土12～15份、玻璃微珠10～14份、高岭土14～7份、珍珠岩12～6份、生石灰10～6份、成核剂10～13份、环保复合型阻燃剂7～10份、聚甲基丙烯酸甲酯7～9份。所述阻燃剂为溴化环氧树脂。本发明专利技术不但具有良好的保温隔热性能、防腐性能和阻燃性能，不易老化，而且绿色环保。

A kind of energy saving and environmental protection material

The invention discloses an energy-saving and environment-friendly material, which is made of sepiolite, diatomite, glass bead, kaolin, perlite, quicklime, nucleating agent, flame retardant and polymethyl methacrylate. The components of the weight fraction were: 18~20 copies, 12~15 copies of diatomite, sepiolite, glass beads, 10~14 copies of 14~7 copies, 12~6 copies of kaolin perlite, lime 10~6, nucleating agent 10~13, environmental protection composite flame retardant 7~10 copies, 7~9 copies of pmma. The flame retardant is brominated epoxy resin. The invention not only has good thermal insulation, anticorrosion and flame retardancy, but also is not easy to age, and is green.

【技术实现步骤摘要】
一种节能环保材料
本专利技术涉及一种保温隔热佳的节能环保材料。
技术介绍
近年来，随着国家经济建设高速发展，国内各行业如化工、石油、轻工、电力等对于保温材料的年需要求日趋增长。特别是国家对于建筑业强制使用优质保温材料的政策，进一步地扩大了国内对保温材料的需求量。不仅产量需求增长，而且在保温材料的各方面的性能指数都有着日益提高的要求，追求无毒无尘无污染，保温隔热性能更加良好。可见，现有技术还有待改进和提高。
技术实现思路
鉴于上述现有技术的不足之处，本专利技术的目的在于提供一种节能环保材料，具有良好的保温隔热性能、防腐性能和阻燃性能。为了达到上述目的，本专利技术采取了以下技术方案：一种节能环保材料，是由以下组分：海泡石、硅藻土、玻璃微珠、高岭土、珍珠岩、生石灰、成核剂、阻燃剂、聚甲基丙烯酸甲酯制作而成。所述的节能环保材料中，所述组分的重量分数分别为：海泡石18～20份、硅藻土12～15份、玻璃微珠10～14份、高岭土14～7份、珍珠岩12～6份、生石灰10～6份、成核剂10～13份、环保复合型阻燃剂7～10份、聚甲基丙烯酸甲酯7～9份。所述的节能环保材料中，所述组分的重量分数是：海泡石19本文档来自技高网...

【技术保护点】
一种节能环保材料，其特征在于，是由以下组分：海泡石、硅藻土、玻璃微珠、高岭土、珍珠岩、生石灰、成核剂、阻燃剂、聚甲基丙烯酸甲酯制作而成。

【技术特征摘要】
1.一种节能环保材料，其特征在于，是由以下组分：海泡石、硅藻土、玻璃微珠、高岭土、珍珠岩、生石灰、成核剂、阻燃剂、聚甲基丙烯酸甲酯制作而成。2.根据权利要求1所述的节能环保材料，其特征在于，所述组分的重量分数分别为：海泡石18～20份、硅藻土12～15份、玻璃微珠10～14份、高岭土14～7份、珍珠岩12～6份、生石灰10～6份、成核剂10～1...