玉米芯发酵基质及其制备方法与应用技术
Corncob fermentation matrix and its preparation methods and Applications
The invention discloses a corn cob fermentation substrate and its preparation method and application. By controlling the physical and chemical properties such as water porosity, aeration porosity and bulk density during the fermentation of corncob, the fermentation end point is determined, and the excellent cultivation substrate is obtained. The time of fermentation culture medium short, physical and chemical properties, the matrix prepared by the method can increase the plant root temperature in winter planting, promote the growth of plants; at the same time, the invention realizes the resource utilization of corn cob, has obvious social benefit and economic benefit and environmental benefit.
【技术实现步骤摘要】
玉米芯发酵基质及其制备方法与应用
本专利技术涉及无土栽培技术，具体地说，涉及一种玉米芯发酵基质及其制备方法与应用。
技术介绍
作为农业大国，我国农产品栽培面积大，在农业生产过程中会产生大量的农业废弃物，如稻谷、小麦、玉米芯、锯末等农作物，给相关的处理部门带来了相当大的工作压力，因此如何有效的处理农业废弃物已经成为我们急需解决的问题。目前，我国对农业废弃物的处理方式较为单一、粗犷，通常是集中焚烧或者就地回填。集中焚烧或者就地回填不仅浪费人力、物力和财力，还对环境造成了极大的污染。将农业废弃物堆肥处理是一种很好的利用方式，目前一般是将其充分腐熟，堆置后的堆肥作为肥料为土壤提供更好的有机质和氮源。但充分腐熟需要的时间长，且不同的农业废弃物初始品质不同，如何在短时间内充分腐熟是堆肥处理的一个难点。特别是如果堆肥完成后如果涉及不同的作物，那么也会有不同的要求。因此，本专利技术通过对玉米芯发酵过程的研究，提出一种栽培基质及其制备方法。
技术实现思路
本专利技术的目的是提供一种玉米芯发酵基质及其制备方法。本专利技术的另一目的是提供所述玉米芯发酵基质在无土栽培技术中的应用。本专利技术...
【技术保护点】
一种制备玉米芯发酵基质的方法，其特征在于，包括以下步骤：1)向玉米芯中添加氮源，调整C:N比至25:1，得物料I；2)向物料I中加入石膏粉，搅拌，将原料的水分含量控制在60％‑65％，得物料II；3)将物料II堆置发酵30‑40天，发酵过程中，每周翻堆一次，保证堆肥内部温度为45‑70℃；4)当发酵材料的理化指标同时达到35％～36％的持水孔隙度，53.7％～53.9％的通气孔隙度，0.35‑0.37g·cm
【技术特征摘要】
1.一种制备玉米芯发酵基质的方法，其特征在于，包括以下步骤：1)向玉米芯中添加氮源，调整C:N比至25:1，得物料I；2)向物料I中加入石膏粉，搅拌，将原料的水分含量控制在60％-65％，得物料II；3)将物料II堆置发酵30-40天，发酵过程中，每周翻堆一次，保证堆肥内部温度为45-70℃；4)当发酵材料的理化指标同时达到35％～36％的持水孔隙度，53.7％～53.9％的通气孔隙度，0.35-0.37g·cm-3的容重，停止发酵，然后将发酵产物干燥，得到玉米芯栽培基质。2.根据权利要求1所述的方法，其特征在于，步骤2)中石膏粉的加入量是玉米芯总质量的0.3％～0.5％。3.根据权利要求1所述的方法，其特征在于，所述方法中还包括发酵前向玉米芯中加入菌剂的步骤。4....
【专利技术属性】
技术研发人员：蒋卫杰，余宏军，高轶楠，李强，
申请(专利权)人：中国农业科学院蔬菜花卉研究所，
类型：发明
国别省市：北京,11
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。